Abstract:In fatigue experiments of NiTi shape-memory alloys (SMAs), TiC inclusions have been found to cause cracks. Based on bending-rotation fatigue (BRF) experiments, which have evolved as one standard method to study the structural fatigue of superelastic NiTi wires, the influence of TiC inclusions on the fatigue behavior of NiTi SMAs has been analyzed quantitatively in this article. Aurichio’s superelastic model was implemented into the finite element (FE) code ABAQUS. One specimen without inclusion and seven specimens with inclusions, at different distances with respect to the neutral axis of the wire specimens, have been analyzed. The stress distributions at the cross sections are nonlinear, and there is a stress plateau in the cross section when the phase transformation occurs. The stress distribution in the cross section of the specimen without inclusion is not only dependent on the load, but also dependent on the loading path and loading history. On the other hand, the maximum stress of the specimen without inclusion is not always at the surface, which is due to the phase transformation behavior of SMAs. The existence of the inclusions changes the stress distributions in the cross section. The maximum stress is dependent on the position of the inclusions, the load, and the loading path. It has been found that the maximum stresses increase as the distance from the inclusion to the neutral axis increases. When the inclusion is at the specimen surface, the maximum stress is the highest among all the studied cases. Such high stresses caused by the inclusions can easily induce fatigue cracks. The simulation can explain the fatigue behavior of BRF experiments and provide a deep insight into the fatigue fracture mechanism of SMAs.

Effect of Specimen Thickness on the Fracture Toughness of a NiTi Shape Memory Alloy

Fracture Behavior of the Compact Tension Specimens in NiTi Shape Memory Alloys

Effect of the Thermomechanical Coupling on Fatigue Crack Propagation in NiTi Shape Memory Alloys

Crack Growth Behavior in NiTi Shape Memory Alloys Under Mode-I Isothermal Loading: Effect of Stress State

Experimental and FEM Analysis of the Fracture Behavior in NiTi Shape Memory Alloys

Investigation on the fracture behavior of shape memory alloy NiTi

Effect of Thermomechanical Coupling on Stress-Induced Martensitic Transformation Around the Crack Tip of Edge Cracked Shape Memory Alloy

Experimental and Numerical Study of the Superelastic Behaviour on NiTi Thin-Walled Tube under Biaxial Loading

Finite Element Simulation of the Influence of TiC Inclusions on the Fatigue Behavior of NiTi Shape-Memory Alloys

Superelastic and Cyclic Response of Nitisma at Various Strain Rates and Temperatures

On the Formation of Martensite in Front of Cracks in Pseudoelastic Shape Memory Alloys

An in Situ TEM Study of the Size Effect on the Thermally Induced Martensitic Transformation in Nanoscale NiTi Shape Memory Alloy

Investigation on the Deformation of TiNi Shape Memory Alloy with a Crack Using Moiré Interferometry

Fracture Toughness Analysis of Anisotropic Nickel-Based Single Crystal Superalloys at High Temperature

On Phase Transition Velocities of NiTi Shape Memory Alloys

Correlation between Hardness Behavior, Shape Memory, and Superelasticity in Ni-Rich NiTi Shape Memory Alloy

Experimental investigation of thermomechanical behaviour of NiTi shape memory alloy under low-velocity impact loading

Quantification of Microscale Factors for Fatigue Failure in NiTi Shape Memory Alloys

Tension-Compression Asymmetry of Single-Crystalline and Nanocrystalline NiTi Shape Memory Alloy: an Atomic Scale Study

Experimental Investigation on Buckling and Post-buckling Behavior of Superelastic Shape Memory Alloy Bars