Abstract:Regular grain oriented (RGO) silicon steels (0.18, 0.23, and 0.28 mm thick) with forsterite coating were formed into 37.2 and 63.6 kg uncut toroids, gapped toroids, and gapped, pressed rectangular cores. During the core (or toroid) manufacturing process, samples of the steel were obtained for Epstein testing at the front and back ends of each core or toroid. The cores/toroids and Epsteins were stress relief annealed at 800° for 4 hours in an 85% nitrogen - 15% hydrogen atmosphere. Additionally, gapped rectangular cores were made from forsterite-coated and stress-coated 0.18, 0.23, and 0.28 mm RGO silicon steels and 0.23 mm stress-coated high-permeability oriented (HGO) silicon steels. Process Factors (PF) were calculated by the equation: PF (%) = \frac{W(core) - W(Epst)}{W(Epst)} \times 100 % For pressed rectangular cores made from RGO steel the process factors improve (i.e. become more negative) with decreasing steel thickness at a given test induction. Comparing gapped rectangular cores, gapped toroids, and uncut toroids, the most negative process factors were obtained in the uncut toroid, reaching as low as about -10% for the 0.18 mm and 0.23 mm RGO steels. For pressed rectangular cores, the high permeability oriented (HGO) silicon steels experienced more positive process factors than the regular grain oriented (RGO) silicon steels. At 1.7T the 29.0Kg cores made from 0.23 mm stress-coated HGO steel had an average process factor of +8.2% while the cores made from stress-coated RGO steel had an average process factor of -1.1%. The differences in core loss seen between Epstein tests of regular grain oriented (RGO) steels and high-permeability grain oriented (HGO) steels are not as large in transformer cores. For transformer manufacturers designing to high loss evaluations (i.e., lower design inductions), RGO steels may be the steels of choice, particularly 0.18 mm thick steel at inductions below 1.5T.

Influence of the stacking method on the iron losses in power transformer cores

Study on Influence of Processing Methods on Loss Coefficients of Iron Loss Model

Optimization of Transposition in Stator Bars of Hydro-Generators

Transversely Isotropic Model of the Stacked Iron Core and its Application in the Design of the Low-Noise Power Transformers

Rotational Core Loss of Silicon Steel Laminations Based on Three-Dimensional Magnetic Properties Measurement

Calculation of core loss under distorted flux density with minor hysteresis loops for laminated steel structure

Optimal Design and Verification of Stacking-Hole in Transformer Core Based on Analysis of Magnetic-Fluid-Thermal Coupling

Predicting Iron Losses in Laminated Steel with Given Non-Sinusoidal Waveforms of Flux Density

Analytical Study and Corresponding Experiments for Iron Loss Inside Laminated Core under Ac-Dc Hybrid Excitation.

Simulation Model for Loss Measurement of Electrical Steel and Study on the Influence of Harmonics

Numerical modeling of magnetic cores with combined electrical steel grades

Comprehensive Magnetic Properties Analysis of the Silicon Steel Considering the Laminated Direction

Iron Loss Separation in High Frequency Using Numerical Techniques

Impact of GOES grade mixing on the iron losses of single-phase magnetic cores

Magnetic Performance Improvement Caused by Tensile Stress in Equivalent Iron Core Fabricated by High-Strength Non-Oriented Electrical Steel

Numerical Study On Ac Loss Of An Hts Coil Placed On Laminated Silicon Steel Sheets With Distorted Ac Transport Currents

Measurements of Iron Loss in PMSM Stator Cores Based on CoFe and SiFe Lamination Sheets and Stemmed From Different Manufacturing Processes

Iron Loss Analysis in Axial Flux Permanent Magnet Synchronous Motors With Soft Magnetic Composite Core Material

Experimental AC loss study on REBCO coil assemblies coupled with an iron cylinder

Methodology and Measurement Setup for Determining PWM Contribution to Iron Loss in Laminated Ferromagnetic Materials

Process factors of transformer cores made from 0.18 mm, 0.23 mm, and 0.28 mm thick grain oriented steel