Heat generation at photopolymerization by multiple-spot exposure with blue light

K Loose,T Niino,T Nakagawa

DOI: https://doi.org/10.1243/0954405991517029

1999-06-01

Abstract:In this paper, heat generation in an acrylate monomer during photopolymerization in multiple-LED photographic curing (MPC) is studied. During the exposure process, an array of multiple beams of light are projected simultaneously on to the resin surface while the projector moves across the resin vat. In this way, exposure occurs through raster scanning. It was found that the heat generated by the polymerization process causes the resin temperature to increase in steps to a maximum of 25 °C when scanning at a velocity of 0.5 mm/s. Heat from the light source itself is not induced. At 3 mm/s, excess temperature decreases to only approximately 4.5 °C. For one layer, three-dimensional temperature profiles show that excess temperature is distributed equally, perpendicular to the scan direction. The polymerization process occurs slowly. Using spectrophotometry, the course of absorbance of the photoinitiators can be observed. At 470 nm, the absorbance increases from 0.4 to 1.2 in the liquid state. The absorbance of the photoinitiators decreases to 0.1. After 30 min of exposure, the polymerization process is complete. This necessitates post-curing after the actual build process.