Abstract:An innovative technology for the direct reduction of copper slag was studied while smelting Cu-Fe alloy by carbon to recover the main valuable elements from the copper smelting slag. The melting temperature of samples first decreased, followed by an increase in Fe3O4 content in slag. The melting temperature reached the minimum temperature of 1157 °C once the Fe3O4 content was about 8 wt%. The recovery rate of copper and iron first increased gradually, followed by a rapid increase in the modifier (CaO). Subsequently, the rise in the recovery rate slowed down. The reduction rate of copper and iron only increased by 1.61% and 1.05% from 5 wt% CaO to 10 wt% CaO, but significantly increased by 8.89% and 14.21% from 10 wt% CaO to 25 wt% CaO, and remained almost unchanged beyond 25 wt% CaO. This could be attributed to the reaction between modifier (CaO) and silicate in acidic copper slag to generate low melting point composite oxide while replacing free iron oxides, improving the melting properties and reduction reaction. Meanwhile, the recovery rates of copper and iron increased with the increase of reaction time, reaction temperature, and reduction agent in a certain range. To obtain good element yield, the optimum conditions for reducing copper and iron from the molten copper slag were determined to be 1500 °C, 14 wt% C, 20–25 wt% CaO, and 60–80 min. The recovery rates of iron and copper reached about 90% and 85%, and the contents of iron and copper in alloy reached about 91–93 wt% and 5–7 wt%, respectively. The tailing was mainly composed of Ca3Si3O9, Ca(Mg,Al)(Si,Al)2O6, and SiO2, which could be used as a raw material for cement and pelletizing.

A Novel Method of Extracting Iron from High-Iron Red Mud and Preparing Low-Carbon Cement Clinker from Tailings

Utilization of Coal Gangue and Copper Tailings As Clay for Cement Clinker Calcinations

Experimental study on utilization of metallic tailings as cement mineralizer and iron raw material

Mechanical Properties and Hydration Mechanism of Iron Tailings–Cement-Based Supplementary Cementitious Materials

Innovative methodology for comprehensive utilization of iron ore tailings: part 2: The residues after iron recovery from iron ore tailings to prepare cementitious material.

A Clean Disposal Method of Carbide Slag with Carbon Emission Reduction: Used As a Flux for Iron Ore Sintering

Investigation of the smelting reduction mechanism and of iron extraction from high-iron red mud

Iron Recovery from Bauxite Tailings Red Mud by Thermal Reduction with Blast Furnace Sludge

Experiments on effect of red mud-based slag on distribution of sulfur in liquid iron

Resource utilization of slag from desulphurization and slag skimming: A comprehensive recycling process of all components

Reduction of Copper Smelting Slag by Carbon for Smelting Cu-Fe Alloy

An efficient and clean utilization technique for red mud based on fluidized bed carbon monoxide reduction

A Thermodynamic and Experimental Assessment of the Recovery of Copper, Iron, Zinc, and Lead from Copper Slag

The harmless and value-added utilization of red mud: Recovering iron from red mud by pyrometallurgy and preparing cementitious materials with its tailings

Novel method for comprehensive utilization of MSWI fly ash through co-reduction with red mud to prepare crude alloy and cleaned slag

A new eco-friendly approach for recovery of iron from copper smelting slag: Using CO2 and Cl2 recycling strategies

A novel approach for the resource utilization of zinc-bearing dust and sludge via the blast furnace main trough

Method for extracting iron from copper smelting waste residue

Modulating red mud for the fabrication of cementitious material by analyzing the thermal evolution of hydrogarnets

Applied Research on Utilization of Metallic Tailings As Clay for Cement Production in Dry Rotary Kiln

Carbothermal reduction of red mud for iron extraction and sodium removal