Abstract:Due to the rapid heating-cooling process and unstable keyhole, pore defects are easily formed during the high energy beam-powder additive manufacturing (AM) process, posing great challenges to the high-performance manufacturing of aerospace components. Using an arc with lower energy density as a heat source can effectively avoid these defects, but its matching raw materials are limited to wire. In this paper, a novel magnetic field assisted powder arc additive manufacturing (MFA-PAAM) method has been proposed, which combines arc heat source and powder raw material to achieve dense metal parts. A transverse magnetic field (TMF) was introduced to solve the powder spattering problem which impacts the stability of the PAAM process, by regulating the direction of the arc plasma flow and the arc pressure. The unique melting behavior of the powder under arc heating was captured by a high-speed camera, which can be summarized into two steps: balling and adsorption by the molten pool. And the well-formed and fully dense Ti60 high-temperature titanium alloy wall components were successfully manufactured using the self-developed equipment. The microstructure of the thin-wall component is dominated by basket-weave distributed α laths and few β sheets remaining at their boundaries. A layered periodic distribution along the building direction was observed, which is mainly distinguished from the content and morphology of the β phase. The average ultimate tensile strength (UTS) and elongation to failure in the travelling direction are 1003.2 MPa and 15.1%, while the average UTS and elongation along the building direction are 1009.3 MPa and 16.6%, respectively. The fracture morphologies in both directions are characterized by ductile fracture. The MFA-PAAM technique shows great potential for fabricating materials that are difficult to be drawn into wires with high efficiency and performance.

Microstructure and Fatigue Properties of Ti-48Al Alloy Fabricated by the Twin-Wire Plasma Arc Additive Manufacturing

Heat Accumulation, Microstructure Evolution, and Stress Distribution of Ti–Al Alloy Manufactured by Twin‐Wire Plasma Arc Additive

Fabrication of γ-TiAl intermetallic alloy using the twin-wire plasma arc additive manufacturing process: Microstructure evolution and mechanical properties

Effect of substrate temperature on microstructure and mechanical properties of TiAl alloy fabricated using the twin-wire plasma arc additive manufacturing system

Composition-induced microcrack defect formation in the twin-wire plasma arc additive manufacturing of binary TiAl alloy: An X-ray computed tomography-based investigation

Twin-wire plasma arc additive manufacturing of the Ti–45Al titanium aluminide: Processing, microstructures and mechanical properties

Fabrication of Fe–30Al alloy using plasma arc welding powered twin-wire directed energy deposition-arc process: Droplet transfer, microstructure, and mechanical property investigation

Microstructural evolution and mechanical property of Ti-6Al-4V wall deposited by continuous plasma arc additive manufacturing without post heat treatment

Microstructure and mechanical properties of Ti-3Al-2V alloy by dual wire + arc additive manufacturing

Electron Beam Welding and Post Heat Treatment of a New Near-Beta High-Strength Ti-4Al-5Mo-5V-5Cr-1Nb Alloy

A novel magnetic field assisted powder arc additive manufacturing for Ti60 titanium alloy: Method, microstructure and mechanical properties

Microstructural Features and Microhardness of the Ti-6Al-4V Alloy Synthesized by Additive Plasma Wire Deposition Welding

Numerical Simulation, Microstructure, and Properties of TC4 Plasma Arc Additive Manufactured Thin Wall

Development of microstructure and mechanical properties of TiAl6V4 processed by wire and arc additive manufacturing

Fabrication of TC4 and Ti48Al bimetals by plasma arc additive manufacturing: Microstructure and mechanical properties

Microstructure Evolution and Mechanical Properties of Wrought/wire Arc Additive Manufactured Ti-6Al-4V Joints by Electron Beam Welding

Microstructure and mechanical properties of twin wire and arc additive manufactured Ni3Al-based alloy

Tensile, Fatigue Properties and Their Anisotropies of Al-Mg Alloy Fabricated by Wire-Arc Additive Manufacturing

Mechanism of enhanced ductility of Ti–6Al–4V alloy components deposited by pulsed plasma arc additive manufacturing with gradient-changed heat inputs

Research on high efficiency deposition method of titanium alloy based on double-hot-wire arc additive manufacturing and heat treatment

In-situ fabrication of Ti<sub>2</sub>AlNb-based alloy through double-wire arc additive manufacturing