Abstract:Over the last few decades, the demand for lightweight constructions has been increased continuously for several industrial applications, like automotive and ship building, to reduce the weight of vessels in order to minimize the CO2 emissions as a result of a lower fuel consumption. Lightweight construction is almost applied for ship applications, especially for yachts, which are designed by using aluminum for the deck constructions and steel for the ship hull. For joining these parts, a high-power laser welding process shall be developed. However, the welding of these dissimilar materials is associated with great challenges, due to the different physical properties and the formation of hard and brittle intermetallic phases, which may influence negatively the properties of the weld seam. The quality of dissimilar joints depends strongly on the mixture ratio between the molten amount of steel and aluminum. However, the mixture ratio varies over the weld seam length due to a high dynamic of the keyhole resulted by welding of this material combination. Furthermore, different batches of materials and varied sheet thicknesses t may influence the mixture ratio. In this study, a high-power laser welding process is developed with in-process control of the penetration depth tP by analyzing the spectral process emissions for dissimilar lap joints of aluminum alloy EN AW-6082 (t = 8 mm) and steel S355 (t = 5–7 mm). In the context of these investigations, an increase of occurring cracks within the weld seam and ejections of molten material with increasing penetration depth tP can be observed. To achieve a relative high joint strength, the penetration depth tP must be kept constant at a value of 1.4 mm. In case of varied batch of material, thickness t of the used sheets, welding speed vS, and leap of the steel sheet thickness t, the penetration depth tP requested cannot be achieved. Using the in-process control of the penetration depth tP, the weld seam quality remains almost constantly over the weld seam length, as shown in visual inspections, metallographic analyses, profiles of the penetration depth tP, and tensile shear testing. Among other things, the appearance of ejections of molten material can be avoided by using the in-process control of the penetration depth tP.

Weldability improvement by wobbling technique in high power density laser welding of two aluminum alloys: Al-5052 and Al-6061

Effects of Laser Beam Wobble on Weld Formation Characteristics, Microstructure, and Strength of Aluminum Alloy/Steel Joints

High-Power Fiber Laser Welding of High-Strength AA7075-T6 Aluminum Alloy Welds for Mechanical Properties Research

Microscopic and Mechanical Properties Characterization of Laser Beam Welded 5754 to 6063 Aluminum Alloys

Systematic approach to improve overlap laser welding of AA5052-H32 with dissimilar thickness by evaluation of mechanical performance, undercut, and welding penetration

The role of filler wire and scanning strategy in laser welding of difficult-to-weld aluminum alloys

Microstructure and Properties of Multilayer 5052 Aluminum Alloy Sheet by Laser Welding

Improving mechanical properties of quasi-continuous-wave laser beam welded 7075 aluminum alloy through microstructural refinement and homogenization of the fusion zone

Experimental investigations on mechanical properties of AA6061-T6 aluminum alloy joined by laser welding using digital image correlation

Effect of activating flux Cr2O3 on microstructure and properties of laser welded 5083 aluminum alloys

Investigations on improving the properties of laser beam welded thick dissimilar joints of steel and aluminum by using filler material

Minimizing defects and controlling the morphology of laser welded aluminum alloys using power modulation-based laser beam oscillation

Fiber Laser Welding Of Similar And Dissimilar Aluminum Alloys

Laser Beam Oscillating Welding of 5A06 Aluminum Alloys: Microstructure, Porosity and Mechanical Properties

Characteristics of Laser-TIG Double-Side Welding for Aluminum Alloys

New insight into microstructure and mechanical properties of heterostructures 7075 Al joint prepared via single mode laser welding

Investigations on in-process control of penetration depth for high-power laser welding of thick steel-aluminum joints

Quantitative analysis of surfaces of cross-section in butt welding of aluminum alloy 5083 using laser–arc hybrid welding

Analysis of Solidification Cracking Susceptibility in Side-by-side Dual-Beam Laser Welding of Aluminum Alloys

Porosity inhibition of aluminum alloy by power-modulated laser welding and mechanism analysis

Laser welding of TC4 titanium alloy to 7075 aluminum alloy with infinite-shape oscillating beam