Effect of activating flux Cr2O3 on microstructure and properties of laser welded 5083 aluminum alloys

Yiming Huang,Yuxue Yuan,Yingchao Feng,Jinping Liu,Lijun Yang,Lei Cui

DOI: https://doi.org/10.1016/j.optlastec.2022.107930

2022-06-01

Abstract:The keyhole was very unstable in the laser welding of aluminum alloys, which was liable to cause welding defects. To solve this problem, the active laser welding (ALW) and the active laser wire filling welding (ALWFW) of 5083 aluminum alloys were investigated with a low laser power. The effect of the activating flux Cr2O3 and process parameters on the weld morphology, the microstructure, the Mg loss, the phase distribution and tensile properties were analyzed. The results showed that the 5083 aluminum alloys with 2 mm thickness were fully penetrated by ALW at a laser power of 1.5 kW. Although the welding process was free of spatter, the weld sagging and the reduction in Mg concentration were serious. With filler wires, the joint morphology changed from concave to flat. In addition, the Mg concentration was supplemented and the β phase was increased. The Al8Cr5 phase generated in the fusion zone was suggested to be the main reason for the increase of the joint strength. The maximum joint strength reached 275 MPa in ALWFW of 5083 aluminum alloys.

optics,physics, applied