Dissimilar joining of low-carbon steel to aluminum alloy with TiC particles added in a zero-gap lap joint configuration by laser welding
Tianyu Xu,Shaowei Zhou,Han Wu,Xiuquan Ma,Huailiang Liu,Meng Li
DOI: https://doi.org/10.1016/j.matchar.2021.111574
IF: 4.537
2021-12-01
Materials Characterization
Abstract:The zero-gap laser lap welding of steel and aluminum with V-shaped grooves on the aluminum surface filled with TiC particles was carried out. The effects of filling with TiC particles of three different sizes (3 μm, 10 μm and 50 μm) on the weld bead morphology, interface phase transformation, steel side grain refinement and mechanical properties of steel‑aluminum joints were explored. Since the particles with diameters of 10 μm and 50 μm were more likely to be dispersed into the molten pool, the joints filled with 10 μm and 50 μm TiC nearly had no defects such as splashes, humps, cracks, etc. that appeared in the joint filled with 3 μm TiC. Interestingly, the Si element enriched at the interface and the larger particle gaps provide more oxygen, resulting in a crystalline SiO2 phase at the interface, especially for the joints filled with 10 μm and 50 μm TiC. Besides, the addition of TiC particles significantly refined the grain at the steel side after solidification and disrupted the established grain orientation, particularly for 10 μm and 50 μm TiC. The addition of 50 μm TiC particles can restrain the intermetallic compound reaction, and some particles are deposited at the steel‑aluminum interface to form connecting nuclei, resulting in a significant improvement for the mechanical properties of the 50 μm TiC filled joints. Fracture morphology analysis revealed that all the samples were mainly brittle fractures, but the joint filled with 50 μm TiC owned a certain degree of plasticity.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing