Abstract:Background: Tungsten (W) is a promising candidate for future use in fusion reactors as plasma facing material. During operation it will be exposed to both particle irradiation and high heat flux (HHF) loads. Particle irradiation, especially helium (He), is expected to cause significant surface modifications of W, might leading to performance degradation. The effect of heat loading can accelerate such surface damage. Therefore, the performance of W under the combined action of both heat and particle fluxes has to be investigated in more detail.Purpose:The aim is to investigate the surface modifications of rolled W during exposure to combined heating and He particle flux depending on surface temperature, He flux and fluence.Methods: The He-flux/heating experiments were performed on rolled W samples using the neutral beam HHF test facility GLADIS at IPP Garching, Germany. HHF loads generated with He atoms of 2.4 MW·m?2 and 9.5 MW·m?2 were used. W samples were adiabatically loaded to peak surface temperatures of ~1000 K, ~2000 K and ~3000 K, close to melting. He fluences increased from about 1×1021m?2 to 6×1022 m?2.Results: During He-loading at a low surface temperature (~1000 K), with increasing fluence, defects appeared in grains first, and then blistering was observed on the sample surface, with many ruptured blisters to form lids and grooves. The largest blisters formed on grains with near <001> surface normal. As fluence was increased continuously, small holes were formed on the surface, and the grooves still existed. However, at intermediate surface temperature (~2000 K), with increasing fluence, the damage morphology changed from a porous structure with blisters,via a porous structure with grooves, to a small coral-like structure. At high surface temperature (~3000 K), an evolution from a porous structure to a coral-like structure with increasing fluence was observed, and the coral-like structure changed little as the increasing of fluence continuously. It is shown that the surface modification of rolled W is dependent on a competitive relationship between the formation of blisters and coral-like structures. To study the behaviour of such He damaged surfaces under fusion relevant transient heat loads, 0.9GW·m?2 Edge Localized Modes (ELMs)-like laser thermal shocks were applied. Local melting was observed on the coral-like structure after thermal shocks.Conclusion: The damage morphology of rolled W changes from blisters with a grain orientation dependence to a porous/coral-like structure with increasing temperature, because at high temperatures the Hen and HenVm (He-vacancy) clusters will be broken up and He will diffuse relatively deeply into the W bulk. This transformation of damage morphology can also be induced by the rise of He fluence.

Helium induced nanoscopic morphology on tungsten under fusion relevant plasma conditions

Fuzz Nanostructure and Erosion on Tungsten–vanadium Alloys Exposed to Helium Plasma in the STEP Linear Plasma Device

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Formation process of tungsten nanostructure by the exposure to helium plasma under fusion relevant plasma conditions

Helium bubble size effects on the surface morphological response of plasma-facing tungsten

Crystal orientation effects on helium ion depth distributions and adatom formation processes in plasma-facing tungsten

Surface Morphology of W Surface Exposed to Low Energy He Plasma at Low Temperature

Helium effects on the surface and subsurface evolutions in single-crystalline tungsten

Deuterium-induced Nanostructure Formation on Tungsten Exposed to High-Flux Plasma

Tungsten Material Behavior under H2, D2, and He Plasma Interaction Conditions in the Framework of Fusion-Relevant Studies

Microstructure Evolution of Pure Tungsten after Low-Energy and High-Fluence He+ Implantation Assessed by Synchrotron Grazing Incidence X-ray Diffraction

Study of Nanostructured Layer Growth on Plasma-Facing Materials Irradiated with Helium Plasma

Nanostructured fuzz growth on tungsten under low-energy and high-flux He irradiation

Response of tungsten surfaces to helium and hydrogen plasma exposure under ITER relevant steady state and repetitive transient conditions

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Hydrogen Behaviors at the Near-Surface Region of Tungsten: A First-Principles Study

He-ion induced surface morphology change and nanofuzz growth on hot tungsten surfaces

The dependence of tungsten fuzz layer thickness and porosity on tungsten deposition rate and helium ion fluence

Micron-Bubble Formation on Polycrystal Tungsten Due to Low-Energy and High-Flux Helium Plasma Exposure

Surface modifications of rolled W during exposure to high heat loads with He

Helium flux effects on bubble growth and surface morphology in plasma-facing tungsten from large-scale molecular dynamics simulations