Synergistic toughening and reinforcement of poly(lactic acid) with epoxy‐terminated hyperbranched polymers
Sudan Zhou,Maolin Guo,Yujuan Jin,Jianjian Sun,Huafeng Tian,Jing Hu
DOI: https://doi.org/10.1002/app.54740
IF: 3
2023-09-30
Journal of Applied Polymer Science
Abstract:Poly(lactic acid) (PLA) was an eco‐friendly and biodegradable material. However, its molecular chain was inflexible and showed limited toughness. In this work, PLA was modified with epoxy‐terminated hyperbranched polymer (EHBP) by melt blending to improve the toughness of PLA. The results showed that epoxy groups within EHBP reacted with carboxyl and hydroxyl groups of PLA, forming chemical micro‐crosslinking. In addition, intermolecular hydrogen bonds were formed between hydroxyl groups on EHBP and PLA, and the combined action of the two ultimately improved the toughness and strength of PLA. Chemical micro‐crosslinking was validated via Fourier transform infrared spectroscopy (FTIR) and gel content analysis. By observing the microscopic morphology of the impact fracture of the blends, it was found that the interface adhesion of the blends increased with the addition of EHBP, enhancing the corresponding mechanical properties. The best interface adhesion was achieved when 2.5 phr EHBP was added to PLA. At this point, compared with neat PLA, the maximum tensile strength, impact strength, elongation at break, and flexural modulus of PLA/EHBP increased by 17.4%, 54.5%, 107.1%, and 25.8% respectively, achieving the goal of simultaneously enhancing the toughness and strength of PLA. The simultaneous improvement in the strength and toughness of PLA expands its potential application value. Poly(lactic acid) (PLA) is an eco‐friendly and biodegradable material. However, its molecular chain was rigid and showed limited toughness. In this work, PLA was modified with epoxy‐terminated hyperbranched polymer (EHBP) by melt blending to improve the toughness. The results showed that epoxy groups within EHBP reacted with carboxyl and hydroxyl groups of PLA, forming chemical micro‐crosslinking. In addition, intermolecular hydrogen bonds were also formed between EHBP and PLA. The combined action of the above two aspects ultimately improved the toughness and strength of PLA. The mechanical property tests results showed that the mechanical properties of PLA improved best when 2.5 phr of EHBP was added. At this point, compared with neat PLA, the maximum tensile strength, impact strength, elongation at break, and flexural modulus of PLA/EHBP increased by 17.4%, 54.5%, 107.1%, and 25.8%, respectively, compared to those of neat PLA. It achieves the goal of simultaneously enhancing the toughness and strength of PLA and subsequently expands its potential application applications.
polymer science