Abstract:The study investigated the microstructure and mechanical properties of composite strengthened high-chromium cast iron by laser quenching and laser shock peening. Observation of microstructure, measurement of microhardness, residual stress and FWHM (full width at half maximum), impact toughness and wear tests were carried out on untreated, laser quenched, laser quench-laser shock peened high-chromium cast iron specimens. The research results showed that the laser shock peening will not produce new phases in high-chromium cast iron, and can further promote the transformation of retained austenite into martensite. The grains inside the laser quench-laser shock peened sample were obviously refined, and the carbides were uniformly dispersed. The laser quench-laser shock peened specimen produced large residual compressive stress and FWHM value on the surface, reaching -432.49 MPa and 2.124°, respectively. The problem of residual stress difference between the hardened zone and the transition zone caused by laser quenching was eliminated, and the tensile stress was all converted into compressive stress, which further increases the dislocation density and improves the micro-hardness. The impact toughness value of laser quench-laser shock peened specimen was 4.43 J/cm 2 , which was 16.27% higher than that of the untreated sample. The friction coefficient and wear rate were significantly reduced, and the wear scar was shallow and narrow, showing weak abrasive wear and oxidative wear, the impact toughness and wear resistance of high-chromium cast iron were improved. The results obtained from this study could be used as reference in future research and applications of laser strengthened high-chromium cast iron.

Study on Laser Surface Hardening Behavior of 42CrMo Press Brake Die

Study on laser surface hardening process of 30CrMnSiNi2A ultra-high strength steel fabricated by laser deposition manufacturing

Structural Characteristics and Sliding Friction Properties of 40CrNiMo Steel after Broadband Laser Hardening

Microstructure and wear behavior of arc-shaped 40CrNiMo steel after laser hardening

Effect of distribution status of the spot matrix on tensile behavior for 42CrMoV when conducting discrete laser surface strengthening: Based on experiment and simulation

Research on 40Cr Laser Quenching Process for Guide Rail

Microstructure distribution and bending fracture mechanism of 65Mn steel in the laser surface treatment

Microstructure and Properties of the Carburize-Quenched Surface After Laser Remelting

Microstructure and mechanical properties of composite strengthened high-chromium cast iron by laser quenching and laser shock peening

Improving the Wear Properties of AISI4130 Steel Using Laser Surface Hardening Treatment

Analysis of Laser Surface Hardening of GM246 Cast Iron

Effect of laser surface hardening on a low carbon steel substrate wear and hardness

Impact wear behavior of laser hardened hypoeutectoid 2Cr13 martensite stainless steel

Local laser softening of press-hardened steel at high feed rates

Effect of laser shock peening on the retention ability of surface roughness in forged Cr5 steel

A Comparative Study of High-Power Diode Laser and CO2 Laser Surface Hardening of AISI 1045 Steel

Laser strengthening of air-cooled diesel engine phosphorus cast iron cylinder liner and its friction & wear properties

Investigation on repairing 30CrMnSiNi2A steel with laser additive and subtractive hybrid remanufacturing technology

Microstructure refinement and properties of 1.0C-1.5Cr steel in a duplex treatment combining double quenching and laser surface quenching

LASER HARDENING PROCESS ON Ck 45 DEPENDING ON THE LASER PARAMETERS - a small review

Surface characteristic and wear resistance of QT-700-2 nodular cast iron after laser quenching combing with shot peening treatment