Abstract:In the microelectronics industry the flip-chip (FC) technology is broadly used to enhance the packaging density. However, the small size and the unique geometry of the FC solder joints induce the electromigration (EM) reliability issue. In this study, a pair of lead-free solder joints (SAC1205) was EM tested by a current of 7.5 103 A/cm2. During the tests, X-ray laminography was applied to observe the microstructure evolution in-situ. Laminography enables the non-destructive observation of the bump microstructure and allows for a quantitative three-dimensional (3D) analysis. After EM testing for 650 h, a new EM failure mechanism was found, differing from the two well-known models, the pancake void propagation and the under-bump-metallization dissolution. Here, a few pre-existing small voids grew and simultaneously many new voids formed and grew over the entire EM testing period. Most of the nucleating voids were distributed in the current crowding region, a few also located in the low-currentdensity region. As the testing time increased, voids increasingly coalesced with each other, forming a porous network which occupied a large part of the interface area and caused the EM failure. A finiteelement (FE) method was then applied to analyze the interplay between the microstructure evolution and current density redistribution. A series of 3D FE models was built based on the laminography images for the different testing stages. The current density distribution from the FE analysis indicates that the formation of discrete voids did not affect the global current density distribution until a major coalescence of the voids occurred. The relieving of the global current crowding in the pancake void model was not found in this new EM failure mechanism. It was the local current crowding around individual void found in the new mechanism that is held responsible for the EM retardation. © 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Experiments on Fluid Mechanics in Flip-Chip Solder Connections

Experimental Study of Void Formation in High-Lead Solder Joints of Flip-Chip Assemblies

Experimental Study of Void Formation in Eutectic and Lead-Free Solder Bumps of Flip-Chip Assemblies

Effect of Reversing Heat Flux Direction During Reflow on Void Formation in High-Lead Solder Bumps

The Two-Phase Flow Simulation and Experimental Research on the Formation of Solder Voids in Power Module

A new prediction methodology for electromigration-induced solder degradation in a WL-CSP system

Experimental and multiphysics simulation study of atoms migration and morphology evolution in solder joints under high current density

Electric Current Effects in Flip Chip Solder Joints

Study of Electromigration-Induced Formation of Discrete Voids in Flip-Chip Solder Joints by In-Situ 3D Laminography Observation and Finite-Element Modeling

Numerical Simulations of Migration and Coalescence Behavior of Microvoids Driven by Diffusion and Electric Field in Solder Interconnects

Coupled Phase Field And Finite Element Modeling Of Void Evolution And Physical Property Change Of Micro Flip-Chip Solder Joints Under Electromigration And Elastic Stress Field

Interfacial Crack Effect on Thermal Mechanical Behavior of Solder Bump for Flip-Chip Package: A Numerical Analysis

Electromigration Mechanism of Failure in Flip-Chip Solder Joints Based on Discrete Void Formation

Study of electromigration-induced formation of discrete voids in flip-chip solder joints by in-situ 3 D laminography

Study of discrete voids formation in flip-chip solder joints due to electromigration using in-situ 3 D laminography and

Phase Field Simulation of Morphological Evolution and Migration of the Microvoid in Small Scale Solder Interconnects Driven by Temperature Gradient

Numerical investigations on the effects of different cooling periods in reflow-soldering process

Effect of Solidification on Solder Bump Formation in Solder Jet Process: Simulation and Experiment

Experimental Investigation on the Height Deviation of Bumps Printed by Solder Jet Technology

Numerical investigation of solder joint shape for micro-spring package during vacuum vapor phase soldering

Study of Migration and Coalescence of Voids Driven by Electric Current Stressing in Solder Interconnects Using Phase Field Simulation