Mesoscopic segregation in H13 steel molten pool during laser remelting: a combined influence of Marangoni convection and oxidation
Jichang Xie,Rija Nirina Raoelison,Yunbo Zhang,Yanan Liu,Wan Shou,Pierre-Emmanuel Mazeran,Nan Kang,Mohamed Rachik
DOI: https://doi.org/10.1016/j.jmatprotec.2023.117956
IF: 6.3
2023-03-23
Journal of Materials Processing Technology
Abstract:Laser-assisted metal processing has received great attention for repair, manufacturing, and surface modification in various industries. However, the mesoscopic segregation and oxidation phenomena during these processes are still obscure. In present work, the H13 tool steel was remelted by a laser beam. The generation of oxide layer, the profile and mesoscopic segregation of molten pool, Marangoni convection, and hardening effect are studied by a combined experimentation and multiphysics coupled simulation approach. An oxide layer was formed on the remelted surface with a thickness of ~ 60 μm in the middle and ~10 μm in the edges. The lightweight elements (Si, V, Cr, and Mn) float upon the molten pool driven by buoyancy and Marangoni convection. In addition, due to their higher redox activity, they tend to have a higher proportion in the oxide layer with respect to the base metal. As a consequence, elemental mesoscopic segregation appeared in the remelted zone. The oxide layer shows an average hardness of 11.8 GPa, which is similar to that of the remelted zone (11.7 GPa). However, the brittleness of the oxide layer leads to cracks, hence deteriorating its mechanical properties. Together, these results bring a further fundamental understanding of mesoscopic segregation that is attributed to the Marangoni convection and oxidation phenomenon during the laser processing of alloys, which might be a critical factor to optimize mechanical properties.
materials science, multidisciplinary,engineering, manufacturing, industrial