Coarsening Transitional Kinetics of Γ′ Precipitates in a Nickel-Based Single Crystal Superalloy During Thermal Exposure
Jiachen Xu,Xinbao Zhao,Wanshun Xia,Lijie Qiao,Yuan Cheng,Hao Liu,Quanzhao Yue,Yuefeng Gu,Ze Zhang
DOI: https://doi.org/10.1016/j.jallcom.2024.175380
IF: 6.2
2024-01-01
Journal of Alloys and Compounds
Abstract:The microstructural stability and coarsening kinetics of gamma ' precipitates in a nickel-based single crystal superalloy (Ni-SX) were thoroughly investigated under various thermal exposure treatments. The evolutions of characteristic parameters including gamma ' size, morphology, area fraction, and gamma channel width were documented. Coarsening rate constants and particle size distributions (PSDs) were calculated and recorded based on measured precipitate sizes at temperatures ranging from 800 degrees C to 1100 degrees C and durations ranging from 100 h to 1010 h. The experimentally derived rate constants were compared with the calculated theoretical values from two mainstream models: matrix-controlled diffusion (LSW model) and interface-controlled diffusion (TIDC model). Notably, transitional coarsening kinetics of gamma ' precipitates from the LSW model to the TIDC model was observed at high temperatures over time. Through a comprehensive consideration of key coarsening kinetics parameters such as elemental diffusivity, trans-interface diffusion coefficient, coarsening rate constant, gamma/gamma ' interfacial area, and solute mass transfer, the transformation of the coarsening kinetics from matrix-controlled diffusion to interface-controlled diffusion was quantitatively discussed. The emergence of the TIDC model as the dominant mechanism was attributed to relatively smaller solute mass transfer through the interface. Moreover, the degradation of gamma/gamma ' interfacial energy and interfacial area, coupled with the increase in solute diffusion coefficient in the matrix, facilitated the trans-interface diffusion to act as a limiting factor throughout the coarsening process.