Abstract:In consolidation of AlON, the extensive decomposition of AlON into α-Al2O3 and AlN during sintering is one of the major reasons that significantly retard its densification process. To accelerate densification of AlON, an ultra-low concentration of La2O3 (0.03 wt%) and Y2O3 (0.02-0.04 wt%) was co-doped as sintering additives to inhibit decomposition of AlON during sintering for fast fabrication of highly transparent AlON ceramics. The phase transformation, microstructure evolution and densification process of the samples undoped and doped additive during heating were studied to investigate the densification mechanism. The results reveal that, compared to the samples undoped additive and single-doped with La2O3, the α-Al2O3 content of the samples co-doped with La2O3 and Y2O3 is significantly deduced at ≤1600 °C, which indicates that the decomposition of AlON is effectively inhibited by co-doping La2O3 and Y2O3. The reduction of α-Al2O3 along with the deceleration effect of La3+ on mass transfer, contributes to more small particles being conserved at high temperatures. Base on this, at later stage of sintering, benefiting from the enhanced mobility of grain boundary by Y3+, AlON ceramics with high relative density (99.79 %) and excellent transparency were obtained via pressureless sintering at 1880 °C for 2.5 h by co-doping 0.03 wt% La2O3 and 0.04 wt% Y2O3. The maximum transmittance of the fabricated AlON ceramics is up to 81.6 % at 3600 nm, and a transmittance of 76.0 % was measured at 400 nm. The ultra-low doping amount of La2O3 and Y2O3 and the high relative density should be the main reasons that lead to the outstanding transparency of the obtained AlON. Additionally, the fabricated AlON ceramics also exhibit a high Vickers hardness of 18.89 ± 0.18 GPa.

ALON and its Composite Ceramics

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

Synthesis of CA6/AlON Composite with Enhanced Slag Resistance

AlON transparent ceramics from powders synthesized by improved direct nitridation

A STUDY ON SYNTHESIS OF AlON BY HOT_PRESS SINTERING

Synthesis technology of AlON

High-pressure Synthesis of Al2O3-cBN Composites: Effect of Thermodynamic Condition and Cbn Volume Fraction on Their Microstructure and Properties

Fabrication of High Strength α-SiAlON/BN Composition Ceramics by Hot Pressing

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Fast pressureless sintering of highly transparent AlON ceramics by reducing Y enrichment with nano-sized granular Y 2 O 3 as additive

Investigation on Mechanical Properties of AlON Ceramics Synthesized by Spark Plasma Sintering

Two-step pressureless sintering of ultrafine powders for the preparation of high strength and transmittance AlON ceramics

Fabrication of highly transparent AlON ceramics by inhibiting decomposition of AlON

Study of the AlON-VN Composite Ceramic

Transparent AlON ceramics by nitriding combustion synthesis precursors and pressureless sintering method

Study on AlON phase evolution and densification behavior as a function of particle size and doping amount

Boron Nitride?Aluminum Nitride Ceramic Composites Fabricated by Transient Plastic Phase Processing

SiC and ZrN Nano-Particulate Reinforced AlON Composites: Preparation, Mechanical Properties and Toughening Mechanisms

RESEARCH ON THE REACTION SYNTHESIS OF AlN-BASED CERAMICS WITH THE ADDITION OF Y2O3

In-situ formation of AlN/Al composite

Compressive properties and failure mechanisms of AlON ceramics under different strain rates