Lei Xie,Qiang Li,Chuntao Chang,Xueru Fan,Aina He,Yuanfei Cai,Qiang Chi,Guan Zhang,Yaqiang Dong
DOI: https://doi.org/10.1016/j.jmrt.2024.05.014
IF: 6.267
2024-05-06
Journal of Materials Research and Technology
Abstract:In this study, the effects of Si content on the glass-forming ability (GFA), thermal stability, annealing window, nanocrystallization process, and soft magnetic properties (SMPs) of Fe 86.3-x Si x B 10 P 2 Cu 1.7 (x = 0, 1, 2, 3, and 4, denoted as Si0, Si1, Si2, Si3, and Si4, respectively) alloys with high Fe and Cu contents were investigated. Moderate addition of Si (x = 1, 2, and 3) enhanced the GFA and suppressed the precipitation of compound phases, thus leading to a large crystallization temperature interval ( ΔT x ) exceeding 185 °C for the alloys. Appropriate addition of Si also resulted in the formation of high-density and fine pre-existing α-Fe nanocrystals in as-spun ribbons and a high growth active energy of α-Fe crystals during the subsequent nanocrystallization process for the Si1, Si2, and Si3 alloys, enhancing competitive growth between α-Fe crystals and resulting in fine nanostructure and excellent SMPs of the nanocrystalline alloys (NAs). As a result, the Si1, Si2, and Si3 NAs obtained by annealing at 420 °C for 30 min exhibited excellent SMPs with saturation magnetic flux density ( B s ) up to 1.84 T and a low coercivity ( H c ) of approximately 10 A/m. In addition, statistical analysis of the relationship between the average grain size ( D ) of α-Fe crystals and H c values of the NAs indicated that an H c α D 3 dependence is observed when the D is less than approximately 30 nm, while this dependence follows the well-known H c α D 6 relationship when the D is above 30 nm. The dependency relationship between D and H c of NAs can guide the selection of an appropriate annealing process to optimize their SMPs.
materials science, multidisciplinary,metallurgy & metallurgical engineering