Effect of localized heat treatment on the weld line shift in deep drawing of tailor welded blanks (TWBs)

Satya Suresh V. V. N.,Srinivasa Prakash Regalla,Ratna Sudheer G.

DOI: https://doi.org/10.1063/1.4963509

2016-01-01

AIP Conference Proceedings

Abstract:This work relates to warm forming of a tailor welded blank (TWB) where in two or more material blanks are welded together and subjected to localized heating before forming to obtain a desired square cup shape. A novel method of selective heating is carried out by using a split punch and a die in which the high strength blank material is subjected to localized heating by the hot punch so as to induce tailored properties by selective heating to soften it thus reducing and controlling the movement of the weld line during forming. TWB sheets which has different thickness/strength need selective heating and cooling to control weld line shift. The stronger material is subjected to localized softening and thereby decreasing the flow stress thus allowing the blank material to flow into the die cavity. Care has been taken so that the heat is not transferred to the weaker blank material otherwise it will lead to further weakening of the part. For this, cooling mechanism is provided by circulating ice water/coolant to the weaker part. The present work is aimed at studying the weld line shift of TWB’s of two different materials namely IFHS and DP 590. Cracks appeared in the weld during forming for drawing ratios greater than 1.7. From the results it was found that the weld line shift is considerably reduced as compared with the results using a single punch. Also it was noticed that there is considerable increase in cup height. Local softening increased the formability of the high strength blank material.