Abstract:A novel Cu direct bonding method is demonstrated using glycerol vapor for its anti‐oxidation and reduction properties. Significantly enhanced bonding quality is evaluated when the low‐cost and eco‐friendly material is applied. This suggests an effective bonding method for semiconductor 3D packaging techniques by replacing costly processes and equipment. As the scaling down of semiconductor devices reaches its physical limits, 3D stacking packaging technology is emerging as a new miniaturization solution. Among the various 3D packaging technologies, Cu direct bonding is widely adopted due to copper's excellent electrical conductivity and the absence of intermetallic compounds for solder bumps. Since copper readily undergoes oxidation, technologies that prevent Cu surface oxidation during Cu direct bonding are essential. However, current research suggests that the methods require additional pretreatment processes, which demand high costs. In this study, a Cu direct bonding method utilizing glycerol vapor is developed to effectively streamline the pretreatment steps. The potential of glycerol as a reducing agent and antioxidant for Cu is demonstrated using a silicon die sample with a size of 10 × 10 mm2, verified through the X‐ray photoelectron spectroscopy. The Cu direct bonding for 3D semiconductor packaging is successfully performed under glycerol vapor atmosphere, without any plasma pretreatment. The cross‐section of the bonded specimens is examined by scanning electron microscopy, and mechanical reliability is assessed by die shear testing.

Cu–Cu direct bonding in air by in-situ reduction of copper oxide with glycerol

Glycerol Vapor Assisted Cu Direct Bonding: Implications for 3D Semiconductor Packaging

Low temperature Cu bonding with large tolerance of surface oxidation

Bonding strength of Cu-to-Cu joints using Cu cold spray deposition by an oxidation and reduction process for power device package

Low temperature Cu–Cu direct bonding in air ambient by ultrafast surface grain growth

Low Temperature Cu/SiO2 Hybrid Bonding with Protruding Copper Pads

Plasma-Activated Cu-Cu Direct Bonding in Ambient for Die-Die and Die-Wafer Bonding

Copper Submicron Particle Pastes with Organic Compounds As Anti-Oxidative Additive for Cu–Cu Bonding in Air

Interfacial Characterization of Low-Temperature Cu-to-Cu Direct Bonding with Chemical Mechanical Planarized Nanotwinned Cu Films

Enhanced Cu-to-Cu direct bonding by controlling surface physical properties

Multi-Die to Wafer Bonding Through Plasma-Activated Cu-Cu Direct Bonding in Ambient Conditions

Low-temperature Cu/SiO 2 hybrid bonding based on Ar/H 2 plasma and citric acid cooperative activation for multi-functional chip integration

Low-Temperature Cu–Cu Direct Bonding Using Pillar–Concave Structure in Advanced 3-D Heterogeneous Integration

Low-temperature Cu/SiO2 Hybrid Bonding Based on Ar/H2 Plasma and Citric Acid Cooperative Activation for Multi-Functional Chip Integration

Low-temperature copper-copper quasi-direct bonding with cobalt passivation layer

Low-temperature Cu Cu Direct Bonding with Ultra-Large Grains Using Highly (110)-Oriented Nanotwinned Copper

Enhanced Cu-Cu bonding for ultrahigh-density interconnection: Co passivation bonding with non-oxidation interfaces

Sintering of Mixed CuAg Nanoparticles Pretreated by Formic Acid Vapor for CuCu Low Temperature Bonding

Low-Temperature Copper Bonding Strategy with Graphene Interlayer

Low Temperature Cu-Cu Bonding Using an Intermediate Sacrificial Sn Layer

Low Temperature Cu-Cu Bonding Using Copper Nanoparticles Fabricated by High Pressure Pvd