Abstract:Optimizing the performance of front silver paste is of great significance in improving the efficiency of the photoelectric conversion of crystalline silicon solar cells. As a conductive functional phase of silver paste, the structure and performance of silver powder have an important influence on the sintering process of silver paste and the conductivity of silver electrodes. Because of their two−dimensional structure, flake silver powders can effectively increase the contact area with other silver powders and silicon cells before sintering. Additionally, flake silver particles have higher surface energy and sintering activity than spherical silver particles of the same particle size. However, recent research has mainly focused on the influence of the particle size of silver powder. This paper fills the research gap regarding the morphology of silver powders and clarifies the influence of flake silver powders on the performance of silver paste. The influence of the ratio of spherical silver powder to flake silver powder in silver paste on the sheet resistance, adhesion, and specific contact resistivity of silver film after sintering at 800 °C was studied, and the optimal ratio was determined according to a cross−sectional contact picture of the silver film. The results showed that with the increase in the mass fraction of the flake silver powder, the sheet resistance of the sintered silver film gradually increased, the adhesion first increased and then decreased, and the specific contact resistance first decreased and then increased. When the flake silver powder content was 0%, the minimum sheet resistance of the silver film was 2.41 m Ω/£. When the flake silver powder content was 30%, the maximum adhesion of the silver film was 6.07 N. When the flake silver powder content was 50%, the minimum specific contact resistivity of the silver film was 0.25 Ω·cm2. In conclusion, when the flake silver powder content was 30%, the comprehensive performance of the silver film was the best.

Low-temperature cured conductive silver paste used for solar cell

Lead-free conductive paste for filament screen printing of solar cells and preparation method of lead-free conductive paste

Preparation of Low Volatile Organic Compounds Silver Paste Containing Ternary Conductive Fillers and Optimization of Their Performances

Screen-Printable Cu–Ag Core–Shell Nanoparticle Paste for Reduced Silver Usage in Solar Cells: Particle Design, Paste Formulation, and Process Optimization

Synthesis of Silver Flakes and Their Application as Conductive Filler for Low-Curing-Temperature Silver Pastes

Novel cocklebur-like nano silver oxide for low-temperature curing pastes with dense conductive paths

Preparation and characterization of low temperature curing conductive silver paste for screen printing

Investigation of 1-hexanol base silver paste formula for low-temperature sintering

Paste Development for an Optimized Filament Stretching Effect During Parallel Dispensing on Transparent Conductive Oxide Layers for Solar Cell Metallization

Effect of Introducing Conductive Organic Carrier on Properties of Low-Temperature Conductive Silver Paste

Optimizing Silver Paste Conductivity with Controlled Convection for Nanowrinkle Growth

Silver frameworks based on self-sintering silver micro-flakes and its application in low temperature curing conductive pastes

Effect of Rheological Property of Silver Conductive Paste on Electrical Property of Si Solar Cells

Low temperature-cured electrically conductive pastes for interconnection on electronic devices

Preparation of Sub-micron Spherical Silver Powders for Solar Cell Paste

Preparation of Superfine Spherical Silver Powders for Solar Cell Silver Paste Via Non-wetting Effect of the Liquid/Solid Interface

Tuning the electrical resistivity of conductive silver paste prepared by blending multi-morphologies and micro-nanometers silver powder

Experimental Investigation of Effect of Flake Silver Powder Content on Sintering Structure and Properties of Front Silver Paste of Silicon Solar Cell

Silver coated copper powder conductive adhesive and preparation method thereof