Abstract:This work investigates the effect of adding SiC nanowires (SiCNWs) on the microstructure and mechanical properties of Mg-2Zn-0.1Y matrix composites under different hot extrusion parameters, and the strengthening mechanism was analyzed. The results showed that as the extrusion temperature elevated from 140 °C to 220 °C or the extrusion speed increased from 0.1 mm/s to 1.0 mm/s, both the dynamic recrystallized grain size and the recrystallized volume fraction increased significantly. The changes of precipitate size and volume fraction exhibited the same trend. The finest recrystallized grains (~0.37 μm) were obtained after extrusion at 140 °C and 0.1 mm/s, which also contained nano-sized MgZn2 precipitates and SiC nanowires. As the extrusion temperature increased from 140 °C to 220 °C at a constant extrusion speed of 0.1 mm/s, the strength of the composites decreased while the elongation improved greatly. Similar change in the strength and elongation were obtained in the composite as the extrusion speed increased from 0.1 mm/s to 1.0 mm/s at extrusion temperature of 140 °C. Meanwhile, these composites exhibited a weakened texture, and a mixture of microcracks and dimples was observed in the fracture surfaces of the as-extruded composites, which explained the mix of brittle-ductile fractures of the composites. The composites extruded at 140 °C and 0.1 mm/s exhibited the best performance with yield strength (YS) and ultimate tensile strength (UTS) of ~495.53 MPa and ~514.18 MPa, respectively. Among all strengthening mechanisms, the proportion of grain refinement strengthening is the highest.

Strengthening and toughening mechanisms of CNTs/Mg–Al composites prepared via powder metallurgy combined with hot extrusion

Enhanced ductility by Mg addition in the CNT/Al-Cu composites via flake powder metallurgy

Evolution of Microstructure and Mechanical Properties of CNTs/Al-Mg Composites Prepared by Powder Metallurgy

Strengthening Ni-Coated CNT/Mg Composites by Optimizing the CNT Content

Study on the Mechanism of CNTs Regulating the Microstructures and Properties of Al–Cu–Mg Alloy

Toughening and strengthening of Cu-coated carbon nanotubes reinforced AZ61 magnesium matrix nanocomposites by improving interfacial bonding

Strengthening and Toughening CNTs/Mg Composites by OpTimizing the Grinding Time of Magnesium Powder

Enhanced strain hardening by bimodal grain structure in carbon nanotube reinforced Al–Mg composites

Effect of Carbon Nanotubes as Reinforcement on the Mechanical Properties of Aluminum-Copper-Magnesium Alloy

Developing Fittingly Comprehensive Performance Carbon Nanotube/Mg-6Zn Sheets with Substantial Enhancement in Formability

Effects of the addition of CNTs and Al alloying on the microstructure and properties of Cu-(Al)/CNTs composites

Study on the Properties of Carbon Nanotube (CNTs) Reinforced AlSi10Mg Composites Fabricated by Powder Metallurgy

Acquiring Mg-Ag microalloying TiB 2 /Al-4.5Cu composite simultaneously with ultrahigh strength and ductility via optimized salt-metal reaction and multistage heat treatment

Design and Preparation of CNTs/Mg Layered Composites

Architectural and component design of CNTs/Al hierarchical composite for enhanced mechanical/thermal properties

The enhanced mechanical properties and strain-hardening capability of CNT/Al composites achieved by heterogeneous micro-laminated architecture

Balanced strength and ductility in CNT/Al composites achieved by flake powder metallurgy via shift-speed ball milling

Effect of hot extrusion on the microstructure and mechanical properties of SiCNWs/Mg-2Zn-0.1Y composite

CNT-induced heterogeneous matrix grain structure in CNTs/Al composites

Combination of enhanced thermal conductivity and strength of MWCNTs reinforced Mg-6Zn matrix composite

Coupling effect of electrophoretic deposition and solid-phase joining on CNTs/Mg multi-material joint