Abstract:In the article, electrochromic WO 3 films were obtained from 25, 100, and 200 mM peroxytungstic acid (PTA) solution. A chronoamperogram of the cathodic reduction of tungsten oxide (WO 3 ) through the stages of formation of a precursor film adsorbed on the surface of the ITO electrode and its subsequent staged reduction to WO 3 and side formation of soluble reaction products is presented. The material yield of the WO 3 film on ITO glass was within 50%, which is due to the parallel occurrence of side processes associated with hydrogen evolution and the reduction of tungsten complexes that were in the precipitation solution (WO 3 reduction scheme). In this case, it was taken into account that thin WO 3 films were the final product. The features of the synthesis of peroxytungstic acid have been studied. It has been shown that the reaction of W dissolution in 37% H 2 O 2 proceeds exothermically. In this case, the reaction temperature reached 96°C within a few seconds, and its decline varied exponentially with the formation of reaction products. The dependence of the limiting current on the square root is obtained. The presented graphic dependence is characterized by linearity, while the beginning of the straight line does not coincide with the origin. The process of intercalation-deintercalation of protons (H + ) (cathode-anode branches of CV) was a consequence of structural and reversible changes as a result of H + intercalation. WO 3 films obtained by electrochemical (cathodic) deposition can be recommended as an electrode material for electrochromic devices (cathode) and as a material for electrochemical sensors. Another promising direction is the development of a wide band gap anode based on WO 3 for photovoltaic devices, which are energy efficient hydrogen generation systems.

Influence of pH Solution on the Electrodeposition of Tungsten Oxide (WO3) Films onto Indium Tin Oxide (ITO)-glass Substrate

Effects of Electrodeposition Electrolyte Concentration on Microstructure, Optical Properties and Wettability of ZnO Nanorods

The Nature of Oxide Films on Tungsten in Acidic and Alkaline Solutions

Electrodeposition of tin oxide thin film from nitric acid solution: the role of pH

Regularities of Obtaining Electrochromic WO3 Films at the Cathode Polarization of the Electrode

Improvement of Electrochromic Performance by Embedding ITO Nanocrystals in Amorphous WO3 Film

Room Temperature Electrodeposition of Ag3PO4Films

Influence of the bath pH value on the microstructure and properties of a novel electrodeposited Ni-W-Ti3C2TX composite coating

Regulation of morphology and visible light-driven photocatalysis of WO3 nanostructures by changing pH

Influence of annealing on microstructure and electrochromic properties of WO3 thin film

Novel Spark Method for Deposition of Metal Oxide Thin Films: Deposition of Hexagonal Tungsten Oxide

Electrodeposition of Sno2 Thin Films from Aqueous Tin Sulfate Solutions

Photocatalysis and photoelectrochemical properties of tungsten trioxide nanostructured films

The Effects of Na2WO4 Concentration on the Properties of Microarc Oxidation Coatings on Aluminum Alloy

Reactive Sputter Deposition of WO3/Ag/WO3 Film for Indium Tin Oxide (ITO)-Free Electrochromic Devices

Effect of pH on the electrodeposition nucleation and growth mechanism of cuprous oxide

Nanostructured WO3 films using high temperature anodization

Tungsten Doped Indium Oxide Thin Films Deposited at Room Temperature by Radio Frequency Magnetron Sputtering

Exploring the impact of a cetyltrimethylammonium bromide surfactant on the electrochemical performance of tungsten oxide thin films

Electrochromic property of tungsten trioxide films prepared by DC magnetron sputtering with oblique angle deposition and thermal oxidation

Electrochemical Deposition and Characterization of Wide Band Semiconductor ZnO Thin Film