Abstract:In the article, electrochromic WO 3 films were obtained from 25, 100, and 200 mM peroxytungstic acid (PTA) solution. A chronoamperogram of the cathodic reduction of tungsten oxide (WO 3 ) through the stages of formation of a precursor film adsorbed on the surface of the ITO electrode and its subsequent staged reduction to WO 3 and side formation of soluble reaction products is presented. The material yield of the WO 3 film on ITO glass was within 50%, which is due to the parallel occurrence of side processes associated with hydrogen evolution and the reduction of tungsten complexes that were in the precipitation solution (WO 3 reduction scheme). In this case, it was taken into account that thin WO 3 films were the final product. The features of the synthesis of peroxytungstic acid have been studied. It has been shown that the reaction of W dissolution in 37% H 2 O 2 proceeds exothermically. In this case, the reaction temperature reached 96°C within a few seconds, and its decline varied exponentially with the formation of reaction products. The dependence of the limiting current on the square root is obtained. The presented graphic dependence is characterized by linearity, while the beginning of the straight line does not coincide with the origin. The process of intercalation-deintercalation of protons (H + ) (cathode-anode branches of CV) was a consequence of structural and reversible changes as a result of H + intercalation. WO 3 films obtained by electrochemical (cathodic) deposition can be recommended as an electrode material for electrochromic devices (cathode) and as a material for electrochemical sensors. Another promising direction is the development of a wide band gap anode based on WO 3 for photovoltaic devices, which are energy efficient hydrogen generation systems.

Regularities of Obtaining Electrochromic WO3 Films at the Cathode Polarization of the Electrode

Electrochromism of titanium oxide thin films

Citric Acid Induced W18O49 Electrochromic Films with Enhanced Optical Modulation

Improvement of Electrochromic Performance by Embedding ITO Nanocrystals in Amorphous WO3 Film

Dual-band Electrochromic Film Based on Mesoporous H-Wo3/o-wo3·h2o/r-tio2 for High Performance Smart Windows

Rapid and low-temperature preparation of tungsten oxide electrochromic thin films by oxygen plasma treatment

Reactive Sputter Deposition of WO3/Ag/WO3 Film for Indium Tin Oxide (ITO)-Free Electrochromic Devices

Growth of a high-performance WO3 nanofilm directly on a polydopamine-modified ITO electrode for electrochromism and power storage applications

Enhanced Electrochromic Performance of Macroporous WO3 Films Formed by Anodic Oxidation of DC-sputtered Tungsten Layers

Improved Electrochromic Performance of WO3 Films with Size Controlled Nanorods

Enhanced electrochromism from non-stoichiometric electrodeposited tungsten oxide thin films

Electrochemical Characteristics of Reconstructed WO3 Electrodes by Embedding ITO Nanocrystals

Optical Characterization of the Coloration Process in Electrochromic Amorphous and Crystalline Wo3 Films by Spectroscopic Ellipsometry

Electrochromic property of tungsten trioxide films prepared by DC magnetron sputtering with oblique angle deposition and thermal oxidation

Enhancement of electrochromic properties using nanostructured amorphous tungsten trioxide thin films

Building Architecture of TiO2 Nanocrystals Embedded in Amorphous WO3 Films with Improved Electrochromic Properties

Topotactic Layer-to-tunnel Crystallization for H-Wo3 Films with Enhanced Electrochromic Performance

Preparation of WO3 Films on Titanium and Graphite Foil for Fuel Cell and Supercapacitor Applications by Electrochemical (Cathodic) Deposition Method

Amorphous/ordered porous crystalline stacked WO3 films fabricated by electrodeposition-assisted sol–gel and its application to electrochromic devices

Electrochromic Properties of Nano-columnar Porous WO<sub>3-x</sub>/TiO<sub>2</sub> Thin Films

Various Coating Methodologies of WO3 According to the Purpose for Electrochromic Devices