Abstract:Grain size engineering, particularly reducing grain size into the nanocrystalline regime, offers a promising pathway to further improve the strength-to-weight ratio of Al alloys. Unfortunately, the fabrication of nanocrystalline metals often requires non-equilibrium processing routes, which typically limit the specimen size and require large energy budgets. In this study, multiple dopant elements in ternary Al alloys are deliberately selected to enable segregation to the grain boundary region and promote the formation of amorphous complexions. Three different fully dense bulk nanocrystalline Al alloys (Al-Mg-Y, Al-Fe-Y, and Al-Ni-Y) with small grain sizes were successfully fabricated using a simple powder metallurgy approach, with full densification connected directly to the onset of amorphous complexion formation. All the compositions demonstrate densities above 99% with grain sizes <60 nm following consolidation via hot pressing at 585 °C. The very fine grain structure results in excellent mechanical properties, as evidenced by nanoindentation hardness values in the range of 2.2-2.8 GPa. Detailed microstructural characterization verifies the segregation of all dopant species to grain boundaries as well as the formation of amorphous complexions, which suggests their influential role in aiding effective consolidation and endowing thermal stability in the alloys. Moreover, nanorods with a core-shell structure are also observed at the grain boundaries, which likely contribute to the stabilization of the grain structure while also strengthening the materials. Finally, intermetallic particles with sizes of hundreds of nanometers form in all systems. As a whole, the results presented here demonstrate a general alloy design strategy of segregation and boundary evolution pathway that enables the fabrication of multiple nanocrystalline Al alloys with hierarchical microstructures and improved performance.

Symbiotically engineered crystalline-amorphous nanostructure in a strong-yet-stable Al alloy with large twinning-induced plasticity

Symbiotic crystal-glass alloys via dynamic chemical partitioning

High-strength and tunable plasticity in sputtered Al–Cr alloys with multistage phase transformations

Inherent and Multiple Strain Hardening Imparting Synergistic Ultrahigh Strength and Ductility in a Low Stacking Faulted Heterogeneous High-Entropy Alloy

Enhancing strength and ductility via crystalline-amorphous nanoarchitectures in TiZr-based alloys

Simultaneous enhancement of strength and ductility via microband formation and nanotwinning in an L12-strengthened alloy

Hierarchical nanostructured aluminum alloy with ultrahigh strength and large plasticity

Multi-scale annealing twins generate superior ductility in an additively manufactured high-strength medium entropy alloy

An order-disorder core-shell strategy for enhanced work-hardening capability and ductility in nanostructured alloys

Coupled solute effects enable anomalous high-temperature strength and stability in nanotwinned Al alloys

Multiscale crack deflection overcomes intermediate-temperature brittleness via hierarchical fiber-like structure in a dual nanoprecipitation-strengthened high-entropy alloy fabricated by selective laser melting

Hierarchical nano-martensite-engineered a low-cost ultra-strong and ductile titanium alloy

Disordered interfaces enable high temperature thermal stability and strength in a nanocrystalline aluminum alloy

Bulk nanocrystalline Al alloys with hierarchical reinforcement structures via grain boundary segregation and complexion formation

Synergistic grain boundary engineering for achieving strength-ductility balance in ultrafine-grained high-Cr-bearing multicomponent alloys

Ultra-strong nanotwinned Al-Ni solid solution alloys with significant plasticity.

Hierarchically ordered coherent interfaces-driven ultrahigh specific-strength and toughness in a nano-martensite titanium alloy

Hierarchical Grain Size and Nanotwin Gradient Microstructure for Improved Mechanical Properties of a Non-Equiatomic CoCrFeMnNi High-Entropy Alloy

Stabilizing defective coherent twin boundaries for strong and stable nanocrystalline nanotwinned Cu

Multi-principal Element Alloys with High-density Nanotwinned 9R Phase

Strength-ductility materials by engineering coherent interface at incoherent precipitates