Abstract:<p>Nanoprecipitates or grain refinement can effectively enhance the mechanical strength of Al alloys, but the room-temperature strengths of precipitation hardened and nanocrystalline Al alloys often fall below 1 GPa. Furthermore, they are largely plagued by precipitous mechanical softening at elevated temperature beyond 300°C, mostly due to degraded microstructural stability. Here, we report a mechanism of combined solute effect in nanotwinned Al-Fe-Ti alloys that enables stability of nanograins up to 400°C and an unprecedented flow stress of ∼ 1.7 GPa at 300°C. The supersaturated Fe solutes in Al act as effective grain refiner, forming superstrong solid solution alloys. More importantly, empirical evidence combined with first principle calculations indicate that the Ti solutes delay the agglomeration of Fe solutes, thereby remarkably extending the temperature window for the stability of nanograins in nanotwinned Al alloys. This study highlights the opportunity to design ultrastrong and stable nanostructured alloys for potential high temperature applications <em>via</em> a combined solute effect.</p>

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: how to design a nano - twinned (NT) Al - Fe - Ti alloy through the coupling solute effect so that it has abnormally high strength and microstructural stability at high temperatures. Specifically, the paper focuses on how to delay the aggregation of Fe solute by introducing Ti solute, thereby significantly improving the stability of the nano - twinned structure at high temperatures and achieving ultra - high high - temperature flow stress. ### Background and Challenges 1. **Limitations of Traditional Aluminum Alloys** - The strength of precipitation - strengthened and nanocrystalline aluminum alloys at room temperature is usually less than 1 GPa. - These alloys will rapidly soften at high temperatures below 300°C, mainly due to microstructural instability. - Nanograins are prone to coarsening at high temperatures, resulting in a decline in material properties. 2. **Deficiencies of Existing Solutions** - Thermal stability can be improved through nano - precipitation or grain - boundary pinning, but these methods are often insufficient to achieve both high strength and thermal stability simultaneously. - The addition of a single solute (such as Fe) can refine grains and improve room - temperature strength, but solute depletion and precipitation are likely to occur at high temperatures, leading to material softening. ### Main Contributions of the Paper 1. **Coupling Solute Effect** - The introduction of Ti solute can delay the aggregation of Fe solute, thereby significantly prolonging the stability of the nano - twinned structure at high temperatures. - Through first - principles calculations, it is found that the presence of Ti makes the Fe - Ti solute pair more stable in the twin boundaries and lattices than the Fe - Fe pair, thus suppressing the aggregation and precipitation of Fe. 2. **Experimental Results** - The NT Al - Fe - Ti alloy still maintains the nano - twinned structure and supersaturated solid - solution state at 400°C (0.72 Tm). - When tested at 300°C, the flow stress of the alloy is as high as approximately 1.7 GPa, much higher than that of traditional aluminum alloys. - High - temperature compression experiments show that the NT Al - Fe - Ti alloy still maintains a high flow stress at 300°C, and significant softening begins to occur at 400°C. ### Conclusion By coupling the Fe and Ti solute effects, the researchers successfully designed a nano - twinned Al - Fe - Ti alloy with abnormally high strength and microstructural stability at high temperatures. This finding provides a new approach for developing ultra - high - strength and stable nanostructured alloys suitable for high - temperature applications.

Coupled solute effects enable anomalous high-temperature strength and stability in nanotwinned Al alloys