Abstract:A long-standing conflict concerning metastable β-titanium (Ti) alloys is that high strength can be achieved through precipitation strengthening of α-phase while plasticity is largely compromised and even lost completely. Such strength-plasticity trade-off severely limits their structural applications. Here, an attempt to address the issue has been made in Ti–6Cr–5Mo–5V–4Al (Ti6554) high-strength metastable β-Ti alloy. Heterogeneous β-structure is architected by partial static recrystallization (SRX) through properly manipulating solution treatment in the hot-rolled bars. The resulting microstructure is composed of the recrystallized ‘new’ equiaxed β-grains (βe) and the remnant elongated β-fibers (βf). This β-morphology dramatically affects the subsequent αs-precipitation behavior during the aging process. αs-precipitation is rather uniform throughout βf-grains because the pre-existing dislocations left by hot rolling provide copious nucleation sites. However, αGB-films are preferentially formed along βe-grain boundaries, which leads to a boundary-affect zone (BAZ) and thereby renders αs-precipitation in a size gradient from β-grain boundaries to grain interiors. As a result, an ultra-high strength of ∼1700 MPa is achieved whilst the ductility can be up to be 5% in the β-hetero aged samples, which is superior to the β-homo aged siblings that have the same strength level but fully succumb to macroscopic brittleness. The enhanced plasticity in the β-hetero aged samples originates from much better deformation compatibility conferred by the aged βf-grains. However, the soft feature of BAZ around βe-grain boundaries in the β-homo aged samples causes strain localization, which eventually induces intergranular brittle fracture. These findings provide an effective strategy for enhancing plasticity of high-strength metastable β-Ti alloys by structural design, where homogeneous αs-precipitates can be easily constructed by combining conventional thermomechanical processing and heat treatment.

Hierarchically ordered coherent interfaces-driven ultrahigh specific-strength and toughness in a nano-martensite titanium alloy

Hierarchical nano-martensite-engineered a low-cost ultra-strong and ductile titanium alloy

Designing ultra-strong and ductile hierarchical titanium alloys via interstitial solute-mediated multi-morphologic α-nanoprecipitates

Trifunctional nanoprecipitates ductilize and toughen a strong laminated metastable titanium alloy

Achieving Enhanced Tensile Strength-Ductility Synergy Through Phase Modulation in Additively Manufactured Titanium Alloys

Making a low-cost duplex titanium alloy ultra-strong and ductile via interstitial solutes

Nature-Inspired Hierarchical Steels.

Additive manufacturing of titanium alloys with enhanced strength and uniform ductility via multi-element alloying

Enhanced strength in pure Ti via design of alternating coarse- and fine-grain layers

α" martensite engineering: A strategy to achieve high yield strength and low yield ratio synergy for dual-phase titanium alloy

Breaking the high-temperature strength-ductility trade-off in TiAl alloys through microstructural optimization

Simultaneously Enhancing the Strength and Ductility of Lamellar Ti–6Al–4V Alloy Via Designing Hierarchical 3D Nanolayered Structure

Introducing β-Ti ductile-zones for enhancing both strength and ductility in heterostructured titanium alloy composites

Superior strength-ductility synergy by microstructural heterogeneities in pure titanium

Hierarchically heterogeneous strategy for Ti 2 AlC/TiAl composite with superior mechanical properties

Achieving high strength-ductility synergy in a hierarchical structured metastable β-titanium alloy using through-transus forging

Enhanced Mechanical Properties of Ti-5Al-5Mo-5V-3Cr-1Zr by Bimodal Lamellar Precipitate Microstructures Via Two-Step Aging

Homogeneous α-precipitation and enhanced plasticity in Ti–6Cr–5Mo–5V–4Al high-strength metastable titanium alloy with heterogenous β-structure

Fabrication of heterostructured Ti alloys with exceptional strength and ductility by direct laser deposition

Heterostructures Enhance Simultaneously Strength and Ductility of a Commercial Titanium Alloy

Nanoscale engineering of low-misfit TiB 2 /Al 3 (Sc,Zr)/α-Al multi-interface to improve strength-ductility synergy for direct energy deposited aluminum alloy