Abstract:The mechanical properties of 3D printed alumina ceramics are degraded due to the micro anisotropy, interlayer interface defects and microporous characteristics. In order to improve its mechanical properties, solid phase sintered, liquid phase sintered and solid-liquid phase sintered alumina (Al2O3) ceramics were prepared by Vat photopolymerization 3D printing technology, respectively. In the experiment, Al2O3 was used as the main material to study the effects of TiO2 solid phase additive, MgO-SiO2 liquid phase additives and TiO2-MgO-SiO2 solid-liquid phase additives on Al2O3 ceramics sintering behavior and mechanical properties, so as to improve the sintering density and mechanical properties of alumina ceramics. The best composition ratio and sintering temperature were determined by shrinkage, relative density, Raman, XRD and SEM characterization. Under optimal sintering conditions, The comprehensive properties of Al2O3 ceramics prepared by liquid phase sintering are more balanced. And has excellent mechanical properties. The flexural strength reached 317 ± 34 MPa and the Vickers hardness up to 1250 ± 102 HV30. Thus, nine types of truss structures are prepared to study their mechanical properties. By changing the structure types, the order of compressive strength is FCC > BCC > DLS. By changing the number of units, the order of compressive strength is 3 × 3 × 3 units >2 × 2 × 2 units >1 × 1 × 1 units. The Al2O3 ceramics prepared by the liquid phase sintering exhibit excellent mechanical compression properties and energy absorption capacity. The FCC structure of 3 × 3 × 3 units can reach 23.2 ± 1.7 MPa compressive strength.

Mechanical characterization of Al2O3 twisted honeycomb structures fabricated by digital light processing 3D printing

Laser powder bed fusion of bio-inspired honeycomb structures: Effect of twist angle on compressive behaviors

3D printing of hollow lattice structures of ZrO2(3Y)/Al2O3 ceramics by vat photopolymerization: Process optimization, microstructure evolution and mechanical properties

Mechanical Properties and Energy Absorption of 3D Printed Double-Layered Helix Honeycomb under In-Plane Compression

Acoustic-assisted DLP 3D Printing Process for Carbon Nanofiber Reinforced Honeycomb Structures

Mechanical Behavior of 3D-Printed Thickness Gradient Honeycomb Structures

3D printed self-similar AlSi10Mg alloy hierarchical honeycomb architectures under in-plane large deformation

Effect of different sintering additives type on Vat photopolymerization 3D printing of Al2O3 ceramics

Formation mechanism and controlling strategy of lamellar structure in 3D printed alumina ceramics by digital light processing

Experimental and Numerical Investigation of Polymer-Based 3D-Printed Lattice Structures with Largely Tunable Mechanical Properties Based on Triply Periodic Minimal Surface

Optimization of printing parameters and out-of-plane compression performance of 316L stainless steel ribbed honeycomb

Preparation of high performance dense Al 2 O 3 ceramics by digital light processing 3D printing technology

Preparation of excellent performance ZTA ceramics and complex shaped components using digital light processing 3D printing technology

Mechanical property enhancement in additively manufactured NiTi double-asymmetric honeycombs with bioinspired graded design

Mechanical properties of Al2O3 and Al2O3/Al with Gyroid structure obtained by stereolithographic additive manufacturing and melt infiltration

Fabrication of alumina ceramics with high flexural strength using stereolithography

Towards high strengthening efficiency of equiaxed and platelet-shaped alumina reinforced zirconia ceramics with textured microstructure using DLP-based stereolithography

Assessment of mechanical performance of Al2O3 ceramic honeycomb sandwich structures produced with SLA 3D-printing regarding unpolymerized slurry removal strategy

Effect of manufacturing process parameters on the compression and energy absorption properties of 4D-printed deformable honeycomb structure

Fabrication of fine and complex lattice structure Al2O3 ceramic by digital light processing 3D printing technology

Microstructure and mechanical properties of 3D printed porous Al2O3–ZrO2 laminated ceramics with tailored porosity