Abstract:To promote the innovation of raw magnesium production technology, an integrated calcination and silicothermic reduction short process for magnesium production was experimentally studied on the laboratory scale in this article. The influences of the thermal decomposition temperature, silicothermic reduction temperature, pelletizing pressures and silicon ratio on the characteristics of producing the magnesium by the short process was studied. The crosslinking effect, including reactions between CO2 decomposed from dolomite and metal elements in ferrosilicon, microstructure change at thermal decomposition and silicothermic reduction stages, was analyzed and discussed. In addition, comparison of the magnesium reduction rate and production efficiency between the new short process and the traditional Pidgeon process was made. The results indicated that the decomposition and reduction temperatures have a more significant influence on the magnesium reduction process than the pelletizing pressure and silicon ratio. A decomposition temperature < 1000 °C and reduction temperature > 1100 °C was proven to be favorable for improving the magnesium reduction rate and production efficiency of the new short process. It was also found that the integrated short process for magnesium production can reach the same total reduction rate and has lower efficiency compared to the traditional process. The decrease of magnesium production efficiency in the new short process was expected to result from reduction of the contact area and hindering of diffusion between CaO·MgO molecules and Si(Fe) atoms because of the microstructure change and ferrosilicon consumption by the reactions between CO2 and metal elements in ferrosilicon. Preparing briquettes with additives of binder or ultrafine particles of raw materials was proposed and considered for further study to improve the production efficiency.

A Study on the Heat Effect during Magnesiothermic Reduction of Porous SiO2

Unlocking the Secrets of Porous Silicon Formation: Insights into Magnesiothermic Reduction Mechanism using In-situ Powder X-ray Diffraction Studies

Preparation of Mesoporous Si Nanoparticles by Magnesiothermic Reduction for the Enhanced Reactivity

Influence of Reactant on Preparation of NiO/SiO_2 Via Adsorption Phase Reaction Technique

The effect of stoichiometric ratio of Mg/SiO2 and annealing on physical properties of silicon nanoparticles by magnesium-thermic chemical reduction process using the SiO2 precursor

Reaction of Mg2+ on the surface of silica in adsorption layer

Magnesium catalyzed growth of SiO2 hierarchical nanostructures by a thermal evaporation process

Key Developments in Magnesiothermic Reduction of Silica: Insights into Reactivity and Future Prospects

Metallothermic Reduction of Silica Nanoparticles to Porous Silicon for Drug Delivery Using New and Existing Reductants

Effect of Sintering Atmosphere on Microstructures and Properties of Synthesized Microporous MgO Refractory Raw Material

From sol–gel prepared porous silica to monolithic porous Mg2Si/MgO composite materials

Preparation of silicon crystallites via controllable thermal reduction of amorphous silica

Mg2Si Promoted Magnesio-Mechanical Reduction of Silica into Silicon Nanoparticles for High-Performance Li-ion Batteries

Energetic characteristics of highly reactive Si nanoparticles prepared by magnesiothermic reduction of mesoporous SiO 2

Experimental Study of Magnesium (Mg) Production by an Integrated Calcination and Silicothermic Reduction Short Process

Effect of a Ca-rich environment on the reaction process of the MgO-activated SiO2 system

Novel Efficient Reduction Route for Magnesium Production Using Silicothermic Process

The Preparation of Magnesium from Magnesia by Using Atmospheric Microwave Al-C Reduction Method

A simple solution calcination route to porous MgO nanoplates