Abstract:316 stainless steel (SS) was coated with CoCrFeNiNbx (x: atomic ratio, x = 0, 0.1, 0.2, and 0.3) high entropy alloy coatings (HEACs) by laser cladding (LC). The impacts of Nb content on the phase composition, microstructure, microhardness, wear resistance and corrosion properties of CoCrFeNi based HEACs were examined. Different from the canonical dendritic (DR) - interdendritic (ID) microstructure presented by the other three HEACs, the ID of Nb0.3 HEACs also existed nanoscale Nb-rich Laves phase composed of Nb-Ni and Nb-Co. The inclusion of Nb significantly reduced the average grain size of CoCrFeNi based HEACs from 59.43 mu m to 11.38 mu m. It also greatly diminished the formation of high angle grain boundaries (HAGBs), increasing the percentage of low angle grain boundaries (LAGBs) from 31 % to 61 %. The microhardness of Nb-containing HEACs was significantly promoted due to the solid solution strengthening and fine grain strengthening caused by large size Nb atoms. Affected by Laves phase with high coordination number and space filling ratio and higher proportion of LAGBs, the microhardness of Nb0.3 HEAC was even as high as 530 HV. The increase in Nb concentration also strengthened the HEACs' resistance to wear. Nb0, Nb0.1, Nb0.2, and Nb0.3 HEACs had corresponding specific wear rates of 0.36, 0.32, 0.23, and 0.20 mm3/Nm. Unlike 316 SS, Nb0 and Nb0.1 HEACs, which had both adhesive wear and abrasive wear, Nb0.2 and Nb0.3 HEACs were mainly wear by abrasive wear. The corrosion behavior of CoCrFeNiNbx HEACs in 0.5 M H2SO4 solution was similar to 316 SS, but the corrosion resistance was stronger than 316 SS. Nb0.3 HEAC with the Ecorr of -164 mV and Icorr of 6.40 x 10-7 A/cm2 showed the best acid corrosion resistance, which could be attributed to the stable and dense passivation film on its surface. Distinct from the intergranular corrosion of other coatings, the corrosion of Nb0.3 HEAC mainly occurred in DR, because the FCC phase acted as the anode site in it when FCC and Laves phase co-existed.

Microstructure and wear properties of nitrided AlCoCrFeNi high-entropy alloy

Electrochemical Corrosion Behavior in Sulfuric Acid Solution and Dry Sliding Friction and Wear Properties of Laser-Cladded CoCrFeNiNb High Entropy Alloy Coatings

Microstructure and mechanical performance of new Al0.5CrFe1.5MnNi0.5 high-entropy alloys improved by plasma nitriding

Microstructures and Mechanical Performance of Plasma-Nitrided Al0.3crfe1.5mnni0.5 High-Entropy Alloys

Effect of Aluminum Content on Plasma-Nitrided Al X CoCrCuFeNi High-Entropy Alloys

Improved tribological behavior of plasma-nitrided AlCrTiV and AlCrTiVSi high-entropy alloy films

Effects of nitrogen content on microstructures and mechanical properties of (AlCrTiZrHf)N high-entropy alloy nitride films

Microstructure, Mechanical Property, and Wear Behavior of NiAl-Based High-Entropy Alloy

Frictional Wear and Corrosion Behavior of AlCoCrFeNi High-Entropy Alloy Coatings Synthesized by Atmospheric Plasma Spraying

Sliding Wear of Spark Plasma Sintered CrFeCoNiCu High-Entropy Alloy Coatings: Effect of Aluminum Addition

Wear and oxidation resistances of AlCrFeNiTi-based high entropy alloys

Microstructure, mechanical and corrosion performance of magnetron sputtered (Al0.5CoCrFeNi)Nx high-entropy alloy nitride films

Nano- and micro-mechanical properties and corrosion performance of a HVOF sprayed AlCoCrFeNi high-entropy alloy coating

Phase Structure, Microstructure, Corrosion, and Wear Resistance of Al0.8CrFeCoNiCu0.5 High-Entropy Alloy

Effect of Microstructure on Wear and Corrosion Performance of Thermally Sprayed AlCoCrFeMo High‐Entropy Alloy Coatings

Wear and high-temperature oxidation resistance of (AlCrFeTiV)100-xNix high-entropy alloy coatings prepared by laser cladding on Ti6Al4V alloy

Effect of Al content on microstructure and wear properties of FeCrNiMnAlx high-entropy alloys

Microstructure, Mechanical Properties, Wear and Erosion Performance of a Novel High Entropy Nitride (AlCrTiMoV)N Coating Produced by Cathodic Arc Evaporation

Influence of Plasma Arc Current on the Friction and Wear Properties of CoCrFeNiMn High Entropy Alloy Coatings Prepared on CGI through Plasma Transfer Arc Cladding

Effect of Nanostructure on Wear and Corrosion Behavior of HVAF-Sprayed Eutectic High-Entropy Alloy Coatings

Effects of Nickel on the Microstructure, Mechanical properties and Corrosion Resistance of CoCrFeNixAl0.15Ti0.1 High Entropy Alloy