Subsonic-Flame-Sprayed CoCrFeNi, AlCoCrFeNi and MnCoCrFeNi-Based High-Entropy Alloy Coatings and Their Tribological Behaviors
Xiaoqian Li,Yidi Wang,Fuguo Wang,Aimin Liang
DOI: https://doi.org/10.1007/s11666-022-01493-y
IF: 2.839
2022-11-23
Journal of Thermal Spray Technology
Abstract:High-entropy alloy coatings (HECs) possess important prospects for tribological applications. In this research, CoCrFeNi, AlCoCrFeNi and MnCoCrFeNi-based HECs were prepared by subsonic flame spraying (SFS) process, which is an extremely convenient and very low-cost thermal spraying technology. The microstructure, phase composition, Vickers hardness, tribological behavior and wear mechanisms (as well as the effect of counterpart ball material, i.e., GCr15 bearing steel or Al2O3) of the HECs were studied under paraffin lubrication. The results indicated that the MnCoCrFeNi-based HEC had excellent tribological behaviors; the lowest friction coefficient (COF) (0.14) and wear rate (3.14 × 10–7 mm3 N−1 m−1) of the MnCoCrFeNi-based HEC were obtained with the GCr15 counterpart, where the dominant wear mechanisms were mild abrasive wear and tribo-oxidation wear. The combination of such factors as the higher oxide content, Vickers hardness and fracture toughness as well as the tribo-oxidation layer formed at the sliding interface significantly improved the wear resistance of the MnCoCrFeNi-based HEC sliding against GCr15 counterpart under micro-vibration reciprocating sliding mode. In contrast, the AlCoCrFeNi and CoCrFeNi-based HECs under the same sliding condition revealed much higher COF value and wear rate as well as quite distinct primary mechanisms of wear, i.e., abrasive, adhesive and tribo-oxidation wear for the AlCoCrFeNi-based HEC, adhesive wear with delamination for the CoCrFeNi-based HEC. When Al2O3 was utilized as counterpart, slight and typical abrasive wear occurred in the MnCoCrFeNi and AlCoCrFeNi-based HECs, respectively, while the primary wear mechanisms of the CoCrFeNi-based HEC changed to severe adhesive wear.
materials science, coatings & films