Microstructure and tribological properties of in-situ M x B reinforced CoCrFeNi HEA composites prepared by laser cladding
Zhongtang Gao,Jinzhou Li,Lingchen Ke,Zhuhui Qiao,Liang Yuan,Zhiming Gao,Chuanwei Zhang
DOI: https://doi.org/10.1016/j.jallcom.2023.171560
IF: 6.2
2023-08-05
Journal of Alloys and Compounds
Abstract:The CoCrFeNiTi x B 2x (x = 0, 0.1, 0.2, and 0.3) high entropy alloy (HEA) composite coatings were prepared on Q235 substrates by laser cladding. The microstructure, grain orientation, precipitated phase and tribological properties of the coatings were investigated by scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), X-ray diffraction (XRD), transmission electron microscopy (TEM) and high-speed reciprocating wear friction tester, respectively. The results show that TiB, Cr 2 B, FeCrB and (FeCr) 2 B phases were in-situ formed in the composite coatings. The microstructures of the coatings are refined and the hardness increases with the addition of Ti and B elements. The grain orientation of all coatings is random. The orientation relationships between the HEA matrix and Cr 2 B is HEA matrix (002) // Cr 2 B ( 1̅3̅1̅ ), HEA matrix [ 5̅ 10] // Cr 2 B [01 3̅ ]. The composite coating exhibits the best wear resistance when the x of CoCrFeNiTi x B 2x is 0.2. The primary strengthening mechanisms of Ti and B doped CoCrFeNi HEAs are the synergistic effect of solid solution strengthening, second phase strengthening and fine grain strengthening.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering