Microstructure and wear resistance of in-situ TiC reinforced AlCoCrFeNi-based coatings by laser cladding

Yutao Li,Kaiming Wang,Hanguang Fu,Xingye Guo,Jian Lin

DOI: https://doi.org/10.1016/j.apsusc.2022.152703

IF: 6.7

2022-05-01

Applied Surface Science

Abstract:High-entropy alloy (HEA) coatings of AlCoCrFeNi are being investigated as potential wear-resistance materials due to their excellent hardness and wear resistance. In this work, AlCoCrFeNi-based coatings were reinforced by in-situ TiC particles via laser cladding. The microstructure and wear resistance were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), and wear resistance tests. In addition, the hardness of oxidation TiC particles was analyzed by first principles calculations. The results show that the dominant phase of AlCoCrFeNi-based coatings is BCC phase. In-situ TiC particles present a flower-shaped morphology with Al2O3 core. Based on the calculated hardness, the hardness of TiC decreases with the increase of oxygen atoms in TiC. The hardness and wear resistance are improved considerably with the generation of the in-situ TiC particles. The AlCoCrFeNi-20% TiC coating exhibits the best wear resistance with an average hardness of 684.4 HV0.3, and the main wear mechanism is abrasive wear.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films

What problem does this paper attempt to address?

The paper mainly explores the effects of in-situ synthesized TiC particles on the microstructure and wear resistance of AlCoCrFeNi-based alloy coatings prepared by laser cladding technology.

The core issue of the paper is to improve the hardness and wear resistance of AlCoCrFeNi high-entropy alloy coatings. The authors added different contents (0%, 10%, 20%, 30%) of in-situ TiC particles to the AlCoCrFeNi-based alloy and used laser cladding technology to prepare the coatings. The microstructure, phase composition, and wear performance of these coatings were studied.

The main findings include:
1. The AlCoCrFeNi-based alloy coatings are mainly composed of disordered body-centered cubic (BCC-A2) phase and ordered body-centered cubic (B2) phase. With the increase of TiC content, a small amount of face-centered cubic (FCC) phase also appears.
2. The in-situ synthesized TiC particles exhibit a flower-like morphology with an Al2O3 core. When the TiC content reaches 30%, the particles present a dendritic structure.
3. With the increase of TiC content, the hardness and wear resistance of the coatings significantly improve. Particularly, the AlCoCrFeNi-20% TiC coating shows the best wear resistance, with an average hardness reaching 684.4 HV0.3.
4. The study also addresses the issue of TiC particle oxidation forming TiC1-xOx solid solutions and uses first-principles calculations to determine the hardness of TiC and its oxides. The results show that as the proportion of oxygen atoms increases, the hardness of TiC decreases.

In summary, the in-situ synthesis of TiC particles can effectively enhance the hardness and wear resistance of AlCoCrFeNi-based alloy coatings, providing theoretical basis and technical support for the development of high-performance wear-resistant materials.