Abstract:Abstract TiAlCoCr x FeNihigh-entropy alloys (HEAs) coatings were fabricated on the surface of Ti6Al4V by laser cladding. Their microstructural evolution with the increase in x value (x = 0, x = 1.0, x = 2.0) was investigated in detail. Besides that, the investigation into the effects of the Cr content on their corrosion behaviors and mechanical properties (in terms of hardness and wear resistance) was also carried out comprehensively. The results indicated that two kinds of phases (a solid solution with thehexagonal close-packed (HCP) structureand Ti 2 Ni) were synthesized in the coatings, and the HCP content was gradually increased with the increase in x accompanied with the decrease in Ti 2 Ni content. A HEA coating only composed of single HCP was successfully prepared when x reached 2.0. The electrochemical and immersion tests all confirmed that the coating with x = 2.0demonstrated the most excellent corrosion resistance in a0.1 mol·L −1 HCl solution from different aspects including corrosion tendency and corrosion rate without the applied potential, the formation difficult/stability of the passive film and the dissolution rate in the passive state, and corrosion surface morphology. The averagemicrohardness values of the coatings weregraduallyincreasedfrom 656HV 0.2 to 800 HV 0.2 with increasing xfrom 0 to 2.0, which wereabout double that of the substrate (350 HV 0.2 ). Wear resistance of the coatings also exhibited the upward tendency with increasing the x values (0.562 mm 3 at x = 2.0, 0.640 mm 3 at x = 1.0, 0.641 mm 3 at x = 0 and 1.419 mm 3 for the substrate). More Cr addition into the cladding material will contribute to the formation of a HEA coating composed of single HCPwith excellent corrosion and wear resistance.

Effects of Ti content on the microstructure and properties of AlCoCrFeNiTix high-entropy alloys prepared by laser cladding

Microstructure and Properties of CoCrFeNiMnTix High-Entropy Alloy Coated by Laser Cladding

Effect of Ti Content on the Microstructure and Corrosion Resistance of CoCrFeNiTix High Entropy Alloys Prepared by Laser Cladding

Microstructure and Friction Properties of CoCrFeMnNiTix High-Entropy Alloy Coating by Laser Cladding

Effect of Ti content on wear and high-temperature oxidation resistances of laser-clad CoCrMoNbTi x high-entropy alloy coating

Cultivating a Comprehensive Understanding of Microstructural Attributes and Wear Mechanisms in FeCrCoNiAlTi x High-Entropy Alloy Coatings on TC6 Substrates Through Laser Cladding Fabrication

Structure and Wear Resistance of TiC-Reinforced Al1.8CrCuFeNi2 High-Entropy Alloy Coating Using Laser Cladding

Microstructures and Wear Resistance of CoCrFeNi2V0.5Tix High-Entropy Alloy Coatings Prepared by Laser Cladding

Investigation into corrosion and wear behaviors of laser-clad coatings on Ti6Al4V

High-temperature oxidation behavior and corrosion resistance of in-situ TiC and Mo reinforced AlCoCrFeNi-based high entropy alloy coatings by laser cladding

Microstructural characterization and corrosion behaviour of AlCoCrFeNiTix high-entropy alloy coatings fabricated by laser cladding

Microstructure and wear resistance of TiAlNiSiV high-entropy laser cladding coating on Ti-6Al-4V

Microstructure and wear resistance of in-situ TiC reinforced AlCoCrFeNi-based coatings by laser cladding

Microstructure and Mechanical Properties of TiC/WC-Reinforced AlCoCrFeNi High-Entropy Alloys Prepared by Laser Cladding

Microstructure and Dry-Sliding Wear Resistance of CoCrFeNiMoTix High Entropy Alloy Coatings Produced by Laser Cladding

Microstructure, thermostability and tribological behavior of composite CoCrFeNiTix high-entropy alloy coatings fabricated by laser cladding

Mechanical and chemical properties of CoCrFeNiMo0.2 high entropy alloy coating fabricated on Ti6Al4V by laser cladding

Effect of ceramic particles on microstructure and properties of CoCrMoNbTi high-entropy alloy coating fabricated by laser cladding

Laser Cladding of FeCoCrNi High-Entropy Alloy on Ti-6Al-4V Alloy: Microstructure, Phase Transformation and Bonding Region

Influence of Al Addition on the Microstructure and Wear Behavior of Laser Cladding FeCoCrNiAlx High-Entropy Alloy Coatings

Crack defects and formation mechanism of FeCoCrNi high entropy alloy coating on TC4 titanium alloy prepared by laser cladding