Cu assisted improvement of wear and corrosion resistance in FeCoNiAl high-entropy intermetallic coating by laser cladding

Jiawang Wu,Fangping Wang,Yaxiong Guo,Xiaojuan Shang,Jing Zhang,Qibin Liu

DOI: https://doi.org/10.1016/j.jmrt.2023.01.003

IF: 6.267

2023-01-07

Journal of Materials Research and Technology

Abstract:High-entropy intermetallic compounds (HEIs) with high strength and outstanding wear resistance are possibly the desirable coating materials. In this present work, A FeCoNiAl HEI composition originated from the multi-component substitution of A site in L1 2 -Ni 3 Al was designed. Next, the HEI coating was achieved using laser cladding. The Cu atoms were incorporated into the HEI coatings to investigate their effects on the phase structure, cracking, and properties of HEI coatings. The results show that the FeCoNiAl HEI coating comprises a sole BCC phase. Adding Cu atoms less than 4.76 at.% does not alter the phase structures. Besides, the study found that as x exceeded 0.3, many tiny rod-like secondary precipitates are generated in the B2 matrix. The study also found that the FeCoNiAl HEI coating hardness at approximately 550 HV 0.2 is twice that of Ni 3 Al coating. The secondary precipitates in the Cu-rich HEI coatings enhance the hardness to about 700 HV 0.2 . Accordingly, the wear resistance shows a similar tendency to the microhardness. Moreover, the Cu 0.4 HEI coating exhibited the lowest friction coefficient (∼0.381) and the narrowest wear scar. In addition, the cracking behavior transforms from transgranular to intergranular cracking due to increased Cu content resulting in decreased cracking sensitivity. The study found that the corrosion resistance of Cu x HEI coatings is more defective than those of Ni 3 Al coating. The Cu atoms effectively decrease the passivation current density of Cu x HEI coatings. The above results provide a novel thought for the development of high-performance coatings.