SYNTHESIS AND PROPERTIES OF INORGANIC COMPOUNDS New Phosphate-Sulfates with NZP Structure
D. Savinykh,S. García‐Granda,A. Orlova,S. Khainakov
Abstract:⎯NaZr2 – xBx(PO4)3 – 2x(SO4)2x (0 ≤ x ≤ 1.25, B = Mg, Co, Ni, Cu, Zn), and NaZr2 – xRx(PO4)3 – x(SO4)x (0 ≤ x ≤ 1.25, R = Al, Fe) phosphate-sulfates series have been prepared by a sol–gel process. These compounds belong to the NaZr2(PO4)3 (NZP) structure family and crystallize in hexagonal crystal system, space group R c. Limited solid solution series were found to exist; their formation temperatures and thermal stability limits were determined. Particle sizes as determined by microstructure observation were 50–200 nm, and for Cuand Zn-containing samples, 200–500 nm. The thermal expansion of phosphate-sulfate NaZr1.25Cu0.75(PO4)1.5(SO4)1.5 was studied in the range 25–700°C. Thermal expansion coefficients and thermal expansion anisotropy were found to be αa = –5.40 × 10–6 °C–1, αс = 18.88 × 10–6 °C–1, αavg = 2.69 × 10–6 °C–1, and Δα = 24.28 × 10–6 °C–1. DOI: 10.1134/S0036023618060207 Design of heat-stress-resistant materials is an important and topical problem of modern materials science [1–5]. These materials can be used in the creation of products for nuclear and space technologies, ceramic pigments, in nuclear technologies for inert fuel matrices and matrices for disposal of radioactive waste, as well as for other applications. Their important properties are thermal stability over a wide temperature range, high thermal conductivity, and no deformation caused by thermal expansion that can lead to destruction. Of these materials, of interest are ceramics based on salt and oxide inorganic compounds. Particular attention should be paid to compounds crystallizing in the NaZr2(PO4)3 (NZP) structure type [6, 7]. These compounds are known for their high thermal stability [2, 8] and some of them for near-zero thermal expansion attained due to a specific heating behavior of the structure consisting in expansion–contraction in different crystallographic directions [3, 9–12]. Not only a low value of the thermal expansion coefficient is important for design of heat “stress” resistant materials, but also low thermal expansion anisotropy is. The structure of NaZr2(PO4)3 and compounds of its family is described by the general crystal-chemical formula (М1)VI(М2) [L (XO4)3], where L and М (М1 and М2) are framework atomic positions and interstitial (extraframework) positions, respectively; VI and VIII denote their coordination surroundings. Positions M can be occupied completely or partially, or they can remain vacant. They are populated mostly by low-charge and relatively large cations, while the [L (XO4)3] framework is built by multicharged cations of small size and negatively charged tetrahedral oxo anions XO4. Various isovalent and heterovalent substitutions, which are typical of the NZP structure [6, 7, 13, 14], create the possibility to tune the properties of compounds in the desired way, specifically thermal expansion characteristics. The thermal expansion model advanced in [6, 10] suggests that the heating behavior of such phosphates depends on the nature of the involved cations (their size, charge, and electronegativity), the major contributors being the weakest bonds. The cations in extraframework positions M and the occupancies of these positions have a greater influence. The following ways are known to reduce thermal expansion parameters in NZP compounds: (1) to increase the radius of an extraframework cation: here, the crystal-chemical principle runs ahead of the thermal one (the position is already expanded due to the residence of a large cation); (2) to reduce the M (interstitial) site occupancy: thereby, the number of cations responsible for thermal deformation is reduced; and (3) to generate solid solutions based on compounds of 3
Materials Science