Abstract:Abstract Y 2 O 3 :Yb 3+ 5 at% ceramics have been synthesized by the reactive sintering method using different commercial yttria powders (Alfa-Micro, Alfa-Nano, and ITO-V) as raw materials. It has been shown that all Y 2 O 3 starting powders consist from agglomerates up to 5–7 μm in size which are formed from 25–60 nm primary particles. High-energy ball milling allows to significantly decreasing the median particle size D 50 below 500 nm regardless of the commercial powders used. Sintering experiments indicate that powder mixtures fabricated from Alfa-Nano yttria powders have the highest sintering activity, while (Y 0.86 La 0.09 Yb 0.05 ) 2 O 3 ceramics sintered at 1750 °C for 10 h are characterized by the highest transmittance of about 45%. Y 2 O 3 :Yb 3+ ceramics have been obtained by the reactive sintering at 1750–1825°C using Alfa-Nano Y 2 O 3 powders and La 2 O 3 +ZrO 2 as a complex sintering aid. The effects of the sintering temperature on densification processes, microstructure, and optical properties of Y 2 O 3 :Yb 3 + 5 at% ceramics have been studied. It has been shown that Zr 4 + ions decrease the grain growth of Y 2 O 3 :Yb 3+ ceramics for sintering temperatures 1750–1775 °C. Further increasing the sintering temperature was accompanied by a sharp increase of the average grain size of ceramics referred to changes of structure and chemical composition of grain boundaries, as well as their mobility. It has been determined that the optimal sintering temperature to produce high-dense yttria ceramics with transmittance of 79%–83% and average grain size of 8 μm is 1800 °C. Finally, laser emission at ∼1030.7 nm with a slope efficiency of 10% was obtained with the most transparent Y 2 O 3 :Yb 3+ 5 at% ceramics sintered.

Chemical Stability of Ceramics Based on Y2.5Nd0.5Al5O12 Oxide with a Garnet Structure in Various Environments

Study of the Hydrolytic Stability of Fine-Grained Ceramics Based on Y2.5Nd0.5Al5O12 Oxide with a Garnet Structure under Hydrothermal Conditions

Radiation resistance of fine-grained ceramics Y2.5Nd0.5Al5O12 under Xe-ions irradiation

Phase Composition, Crystal Structure and Microwave Dielectric Properties of Nb-Doped Yttrium Aluminum Garnet Ceramics

Mechanical Properties and Thermal Shock Resistance of Fine-Grained Nd:YAG/SiC Ceramics

Alpha-particle irradiation effects of Nd-doped Y3Fe5O12 ceramics

Phase composition, microstructure, and microwave dielectric properties of non-stoichiometric yttrium aluminum garnet ceramics

On the solubility of Nd3+ in Y3Al5O12

Synthesis of Nd3+ Doped Nano-Crystalline Yttrium Aluminum Garnet (YAG) Powders Leading to Transparent Ceramic

The influence of Gd doping on thermophysical properties, elasticity modulus and phase stability of garnet-type (Y1-xGdx)3Al5O12 ceramics

Phase evolution and chemical stability of Nd‐doped Y 3 Fe 5 O 12 waste forms synthesized in molten salt at a low temperature

Phase composition, crystal structure, and microwave dielectric properties of Nb-doped and Y-deficient yttrium aluminum garnet ceramics

Influence of Ph Values on (nd+y):Al Molar Ratio of Nd:YAG Nanopowders and Preparation of Transparent Ceramics

Microstructure and Mechanical Properties of Al2O3/YAG Eutectic Ceramic Grown by Horizontal Directional Solidification Method

Synthesis of Nanostructured Nd:Y2o3 Powders by Carbonate-Precipitation Process for Nd:Yag Ceramics

Heat conductivity of YAG:Nd + Mo ceramic composites obtained by Spark Plasma Sintering

Phase Stability and Thermal Expansion Property of ZrO2–NdO1.5–AlO1.5 Ceramics from 50 to 1550 °C

Effects of Al substitution on dielectric response and magnetic behavior of yttrium iron garnet ceramics

Influence of Yb 3+ Doping on Phase Stability and Thermophysical Properties of (Y 1-X Yb X ) 3 Al 5 O 12 under High Temperature

Ionic Occupation, Structures, and Microwave Dielectric Properties of Y3MgAl3SiO12 Garnet‐type Ceramics

Effect of starting materials and sintering temperature on microstructure and optical properties of Y2O3:Yb3+ 5 at% transparent ceramics