Investigation of the microstructure of the fine-grained YPO$_4$:Gd ceramics with xenotime structure after Xe irradiation

D.A. Mikhailov,E.A. Potanina,A.V. Nokhrin,A.I. Orlova,P.A. Yunin,N.V. Sakharov,M.S. Boldin,O.A. Belkin,V.A. Skuratov,A.T. Isatov,V.N. Chuvil'deev,N.Y. Tabachkova

DOI: https://doi.org/10.3390/ceramics5020019

2022-03-26

Abstract:The paper reports on the preparation of xenotime-structured ceramics by the Spark Plasma Sintering (SPS) method. Phosphates Y$_{0.95}$Gd$_{0.05}$PO$_4$ (YPO$_4$:Gd) were obtained by the sol-gel method. The synthesized nanopowders are collected in large agglomerates 10-50 mkm in size. Ceramics has a fine-grained microstructure and a high relative density (98.67%). The total time of the SPS process was approximately 18 min. High-density sintered ceramics YPO$_4$:Gd with a xenotime structure were irradiated with Xe$^{+26}$ ions (E = 167 MeV) to fluences of $1\times10^{12}$-$3\times 10^{13}$ cm$^{-2}$. Complete amorphization at maximum fluence was not achieved. As the fluence increases, an insignificant increase in the depth of the amorphous layer is observed. According to the results of grazing incidence XRD (GIXRD), with an increase in fluence from $1\times10^{12}$-$3\times 10^{13}$ cm$^{-2}$, an increase in the volume fraction of the amorphous structure from 20 to 70% is observed. The intensity of XRD peak 200 YPO$_4$:Gd after recovery annealing (700$^\circ$C, 18 h) reached a value of ~80% of the initial intensity I0.

Materials Science

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to study the microstructural changes of fine - grained YPO₄:Gd ceramics after xenon irradiation, especially the radiation resistance of this material under high - dose irradiation and its recovery properties. Specifically, the authors prepared Y₀.₉₅Gd₀.₀₅PO₄ (YPO₄:Gd) ceramics with a monoclinic pyroxene structure by spark plasma sintering (SPS) technology and carried out xenon ion (Xe⁺²⁶) irradiation experiments on them to evaluate their structural stability and radiation resistance under high - dose irradiation conditions. In addition, the possibility of restoring the crystallinity of irradiated samples by annealing treatment was also studied.

### Background and Objectives of the Paper
1. **Background**:
- Compounds with a monoclinic pyroxene structure are potential actinide immobilization matrices.
- These compounds have good self - irradiation resistance, high melting points and hydrolysis stability.
- It is difficult to obtain high - density monoclinic pyroxene - structure ceramics by traditional sintering methods, while the SPS technology can achieve high - density sintering at lower temperatures and in shorter times.

2. **Objectives**:
- Prepare high - density Y₀.₉₅Gd₀.₀₅PO₄ (YPO₄:Gd) ceramics by SPS technology.
- Study the influence of xenon ion irradiation on the microstructure of YPO₄:Gd ceramics, especially the amorphization phenomenon caused by irradiation.
- Evaluate the possibility of restoring the crystallinity of irradiated samples by annealing treatment.

### Experimental Methods
1. **Material Preparation**:
- Synthesize Y₀.₉₅Gd₀.₀₅PO₄ powder by the sol - gel method.
- Sinter the powder using SPS technology under vacuum conditions to prepare ceramic samples with a diameter of 10 mm and a height of 3 mm.

2. **Irradiation Experiment**:
- Irradiate ceramic samples with high - energy (167 MeV) xenon ions on the IC - 100 FLNR JINR cyclotron, with an irradiation flux of 1×10¹² to 3×10¹³ cm⁻².

3. **Characterization Methods**:
- **X - ray diffraction (XRD)**: Analyze the phase composition of powders and ceramics.
- **Grazing - incidence X - ray diffraction (GIXRD)**: Study the microstructural changes of the surface layer after irradiation.
- **Scanning electron microscope (SEM)** and **Transmission electron microscope (TEM)**: Observe the microstructure of powders and ceramics.
- **Density measurement**: Measure the density of ceramics by the hydrostatic weighing method.
- **Annealing experiment**: Study the possibility of restoring the crystallinity of irradiated samples by annealing treatment.

### Main Results
1. **Phase Composition and Microstructure**:
- Through XRD analysis, it was confirmed that the prepared YPO₄:Gd powders and ceramics are all single - phase and have a monoclinic pyroxene structure.
- SEM and TEM observations show that the powder is composed of aggregates of nanoparticles, and the ceramic has a high - density fine - grained microstructure.

2. **Irradiation Effects**:
- Irradiation causes partial amorphization of the surface layer of YPO₄:Gd ceramics, but not complete amorphization.
- As the irradiation dose increases, the XRD peak intensity gradually decreases, indicating an increase in the degree of amorphization.
- The amorphization phenomenon of the surface layer was further confirmed by GIXRD analysis.

3. **Annealing Recovery**:
- After annealing treatment, the crystallinity of the irradiated samples is partially recovered, and the XRD peak intensity is restored to about 80% of the initial value.

### Conclusion
This study successfully prepared high - density YPO₄:Gd ceramics by SPS technology and evaluated their radiation resistance through xenon ion irradiation experiments. The results show that YPO₄:Gd ceramics exhibit good structural stability under high - dose irradiation, and the amorphization caused by irradiation can be partially recovered by annealing treatment. These results provide an important reference for the development of nuclear waste immobilization materials with high radiation resistance.