Radiation resistance of fine-grained ceramics Y2.5Nd0.5Al5O12 under Xe-ions irradiation

Alekseeva L.S.,Nokhrin A.V.,Yunin P.A.,Nazarov A.A.,Orlova A.I.,Skuratov V.A.,Issatov A.T.,Kovylin R.S.,Murashov A.A.,Boldin M.S.,Voronin A.V.,Chuvil'deev V.N.,Zotov D.A.

2023-12-10

Abstract:Oxide Y2.5Nd0.5Al5O12 (YAG:Nd) with garnet structure was synthesized in the powder and ceramics forms. Fine-grained YAG:Nd ceramics with a relative density of ~99% were obtained by the Spark Plasma Sintering method (SPS). The radiation resistance of ceramics was studied under irradiation with swift Xe-ions (E = 146 MeV). A gradient defect structure is formed in irradiated ceramics, varying from layer to layer. The strained YAG phase formed as a result of Xe ions irradiation is localized in a near-surface layer with a thickness of ~5 {\mu}m. Full amorphization of the samples was observed under irradiation with a fluence of 1x10^13 cm-2. The calculated critical fluence was 6.5x10^12 cm-2, which corresponded to 0.03 dpa. The microhardness of the surface layers of irradiated ceramics is less than the central layers, and, in general, decreases with increasing ion fluence.

Materials Science

What problem does this paper attempt to address?

The paper aims to study the radiation resistance of fine-grained ceramics based on Y₂.₅Nd₀.₅Al₅O₁₂ (YAG:Nd) oxide under xenon ion irradiation. Specifically, the paper focuses on the following aspects:

1. **Material Preparation and Characteristics**:
- High-density fine-grained YAG:Nd ceramics were prepared using the Spark Plasma Sintering (SPS) method.
- The microstructure, phase composition, and density of the ceramics were studied.

2. **Radiation Testing**:
- The ceramic samples were irradiated with xenon ions at an energy of 146 MeV to study their behavior under different irradiation doses.
- The lattice deformation and amorphization phenomena of the ceramics during irradiation were investigated.

3. **Key Findings**:
- It was found that YAG:Nd ceramics begin to exhibit lattice expansion and partial amorphization at certain irradiation doses.
- The critical irradiation dose for complete amorphization was calculated to be 6.5 × 10¹² cm⁻², corresponding to 0.03 dpa.
- The change in microhardness of the ceramic surface layer after irradiation was studied, revealing a decrease in microhardness with increasing irradiation dose.

4. **Conclusion**:
- The radiation resistance of YAG:Nd ceramics under xenon ion irradiation was determined through experiments, and the changes in their microstructure were revealed.
- Microhardness measurement techniques can be used to monitor the degree of radiation damage to the ceramic surface layer.

In summary, this paper mainly explores the radiation resistance and microstructural changes of fine-grained YAG:Nd ceramics under high-energy xenon ion irradiation, which is of great significance for the development of new inert matrix fuels.