In-situ aqueous phase hydrodeoxygenation of methyl palmitate on Ni-Co alloy embedded in mesoporous carbon hollow spheres catalysts

Shangzhen Feng,Hantao Zhou,Zhongze Wang,Sihao Shu,Xing Zhang,Jixiang Chen
DOI: https://doi.org/10.1039/d3nj04975b
IF: 3.3
2024-03-16
New Journal of Chemistry
Abstract:Herein, the Ni-Co alloy embedded in mesoporous carbon hollow spheres (MCHS) catalysts were prepared by the one-pot Stöber method using SiO2 as hard template and resorcinol-formaldehyde resin (RF) as carbon source, and they were tested for in-situ aqueous phase hydrodeoxygenation of methyl palmitate to hydrocarbons using methanol as hydrogen donor. The formation of the catalyst precursors involves nucleation, growth and co-assembly of RF and SiO2. The introduction of SiO2 can construct the mesoporous and hollow structure and improve the specific surface area. It also reduces the micropore volume due to the reduced graphitization degeree of the catalysts induced by SiO2. Thus, the internal diffusion resistance is decreased. Particularly, the Ni-Co alloy particles formed during the carbonization are embedded in the mesoporous carbon layer, effectively hindering their sintering and leaching under the harsh hydrothermal condition. Moreover, the metal sites can be exposed on both mesoporous channels and inner/outer surfaces of the carbon hollow spheres, making the reactants easily accessible. In the in-situ hydrodeoxygenation of methyl palmitate, the as-prepared catalyst gives the pentadecane yield of 89.0% at 310 °C for 1 hour. It is notably that the facile diffusion in MCHS suppresses the undesired C-C bond hydrogenolysis. The catalyst is not obviously deactivated during five reactions.
chemistry, multidisciplinary
What problem does this paper attempt to address?