Abstract:Titanium silicide (TiSi2) thin films were prepared on glass substrate by atmospheric pressure chemical vapor deposition using SiH4 and TiCl4 as the precursors. The phase structure of the thin films was identified by x-ray diffractometry. The surface morphology and thickness of the thin films were observed by field emission scannig electron microscopy and the sheet resistance of the thin films was measured using the four point probe method. The results show that the TiSi2 thin films are formed in a face-centered orthorhombic structure. Due to the influence of the amorphous glass substrate, an amorphous layer is initially formed on the substrate and the TiSi2 crystalline phase grows on top of it. As the thickness and content of TiSi2 crystalline phase increase with deposition time, the resistivity of the thin film decreases. Besides, the growth rate and thus the size of TiSi2 crystalline phase increase as the deposition temperature increases. The stack density decreases when the deposition temperature increases above 700°C because the rapid growth at the higher temperatures causes more irregular shape of crystalline particles. The maximal stack density of the crystalline phase and thus the minimum resistivity of the thin films are obtained at the deposition temperature of 700°C. The expressions of the stack density of crystalline phase and the resistivity of the thin films as functions of the deposition conditions are theoretically deduced which are well consistent with the experimental results.

Reactive-sputter-deposited TiN films on glass substrates

Crystallographic Orientation Dependence of Dielectric Response in Lead Strontium Titanate Thin Films

Study of Titanium Nitride for Low-E Coating Application

Study of optical and electrical properties of TiN thin films prepared by cathodic ion sputtering

The Structure and Properties of V Doped TiN Films Prepared at Various Temperatures

Electrical and optical properties of titanium nitride coatings prepared by atmospheric pressure chemical vapor deposition

Influence of Substrate Bias on Properties of TiN Films with X-ray Photoelectron Spectroscopy and Atomic Force Microscopy Studies

Structure, Electrical and Optical Properties of TiNx Films by Atmospheric Pressure Chemical Vapor Deposition

Formation Of Nanocrystalline Tin Film By Ion-Beam-Enhanced Deposition

Preferentially orientated E-beam TiN thin films using focused jet of nitrogen gas

Growth and mechanical anisotropy of TiN thin films

Properties and morphology of TiN films deposited by atomic layer deposition

Surface Conductivity and Preferred Orientation of TiN Film for Ti Bipolar Plate

Nucleation and Growth of Tisi2 Thin Films Deposited on Glass by Atmospheric Pressure Chemical Vapor Deposition

APCVD Prepared TiNxOy Films with Energy-Saving and Self-Cleaning Functions

The Behavior of Crystalline Grain Growth in TiNi Shape Memory Alloy Thin Films

Investigation of microstructure evolution in Pt-doped TiO2 thin films deposited by rf magnetron sputtering

TiO2 films prepared by DC reactive magnetron sputtering at room temperature: Phase control and photocatalytic properties

Nanohardness of nanocrystalline TiN thin films

Orientation Preferred Structures in BaTiO3 Thin Films on Ni Substrates

Preparation of (001) preferentially oriented titanium thin films by ion-beam sputtering deposition on thermal silicon dioxide