Microstructure, Mechanical, and Corrosion Properties of Mg-Zn-Ga Alloy after Hot Rolling

S. O. Rogachev,V. E. Bazhenov,A. A. Komissarov,A. V. Li,N. E. Munzaferova,S. V. Plegunova,D. V. Ten

DOI: https://doi.org/10.1007/s11665-024-09361-2

IF: 2.3

2024-03-27

Journal of Materials Engineering and Performance

Abstract:The effect of hot rolling on the structure and mechanical properties of the Mg-2Zn-2Ga (wt.%) alloy has been studied. The original cast alloy plates after heat treatment were subjected to rolling from an initial thickness of 7 mm to a final thickness of 0.3 mm at three temperatures, namely 200 °C, 300 °C, and 400 °C. Optical and scanning electron microscopy, microhardness measurement, tensile testing, and corrosion testing were used to characterize the material. It has been established that during rolling at temperatures of 200 and 400 °C, the structure formation proceeds through the formation of shear bands, and at a temperature of 300 °C it proceeds through the twinning and dynamic recrystallization mechanisms. The highest strength of the alloy was obtained after rolling at 300 or 400 °C to reduction up 94-95%: the yield strength and ultimate tensile strength were 247-264 and 273-305 MPa, respectively, and the elongation was 2-5%. Heat treatment (annealing) of the rolled alloy improves its ductility (relative elongation increases to 9-16%). The corrosion resistance of the alloy was determined by hydrogen evolution corrosion test in Hank's solution at 37 °C and immersion time of 192 h. The alloy after rolling had a corrosion rate of 0.41 mm/year, but post-rolling heat treatment promotes a decrease in corrosion rate to 0.15-0.28 mm/year.

materials science, multidisciplinary