Abstract:In the present work, the influence of number of cycles on microstructure, texture and mechanical behavior of Zr702 plates has been systematically studied using the accumulative roll bonding (ARB) method. Electron back-scatter diffraction and transmission electron microscopy have been used to study the development of microstructure and texture. Results show that the {0001} bimodal texture is obvious in all the samples. At the same time, the fiber is weakened and the fiber is strengthened gradually with the increase of ARB cycle number from 1 to 3. In addition, some unbroken coarse grains with c-axis close to normal direction can be observed in ARB samples. The reason for this phenomenon is that the prismatic slips are not easily activated due to unfavorable orientation. The tensile test results along the rolling direction show that the strength increases and the elongation decreases with the increase of ARB cycle number. Compared with the as-received plate sample, the yield strength of ARB sample subjected to 3 cycles is increased by about 99%, while still maintain 7.4% of the elongation to fracture. In order to clarify the mechanical mechanisms during deformation, the back stress hardening caused by the heterostructure mixed with coarse and fine grains and substructure have been discussed in detail. In addition, the calculation results of Schmid factor (SF) show that prismatic slip is the dominant slip mechanism in the deformation process of all samples. However, the average SF value of the basal slip systems decreases with the increasing number of ARB cycles, which maybe another significant factor leading to the change of yield strength.

A Two-Scale Texture Modelling of AA1050 Aluminum Alloy after Accumulative Roll-Bonding (ARB)

Role of Strain Path Change on Texture and Microstructure of Accumulative Roll-Bonding (ARB) Processed Aluminum: A Comparative Study of Unidirectional and Reverse ARB

Evolution of texture and microstructure during accumulative roll bonding of aluminum AA5086 alloy

Texture and Mechanical Anisotropy of Ultrafine-Grained Aluminum Alloy AA6016 Produced by Accumulative Roll Bonding

Abnormal texture evolution of accumulative roll bonded Al-Cu by adding alumina particles

Analysis of the Strain Distribution and Texture Measurements in Asymmetric Rolling (AR) and Asymmetric Accumulative Roll Bonding (AARB)

Stoichiometry and Texture Evolution of Individual Layers during Accumulative Roll Bonding of Al-Mg Laminated Composites

Developing Alternative Texture in a 90Cu-10Zn α-Brass Alloy via Route Changes in Accumulative Roll Bonding Process

Microstructure and Texture Evolutions of Aa1050 Aluminum Alloy Cold Rolled to High Strains

Analysis of Through-Thickness Heterogeneities of Microstructure and Texture in Nickel after Accumulative Roll Bonding

Revealing the evolution mechanisms of microstructure, texture and mechanical behavior in Zr702 alloy plates fabricated by accumulative roll bonding

Texture Development of Arb Processed Mg/Al Multilayers

Modeling Texture Evolution During Rolling Process of AZ31 Magnesium Alloy with Elasto-Plastic Self Consistent Model

Texture Evolution of the Mg/Al Laminated Composite by Accumulative Roll Bonding at Ambient Temperature

Through-thickness variations of microstructure and texture in nickel processed by accumulative roll bonding

Evolution of Microstructure, Texture and Mechanical Properties for Multilayered Al Matrix Composites by Accumulative Roll Bonding

On the Relationship between Thermomechanical Processing Parameters and Recrystallization Texture in AA1100 Aluminum Alloy

Microstructure Evolution and Mechanical Properties of AZ31 Alloy with Accumulative Roll Bonding

Evolutionoftexture in Cu-Nb multilayer composites fabricated viaaccumulative roll bonding

Effect of Low Temperature Annealing on Surface Shear Textures of Aluminum Sheet Processed Accumulative Roll Bonding

TEXTURE EVOLUTION OF POLYCRYSTALLINE ALUMINUM DURING ROLLING DEFORMATION I.Experimental Study