New insight of texture and microstructure evolution, and the connections between with tensile performance in as-annealed Al-Cu-Mg-Zr sheet
Fanghua Shen,Zhenzhong Sun,Wenfang Li,Zirong Zhou,Jianwen Guo,Yang Hai,Yuliang Zhao,Yuxun Zhang,Jiaen Luo,Yongsen Deng,Xinhao Zhao,Boyan Sun,Danqing Yi
DOI: https://doi.org/10.1016/j.jallcom.2023.171784
IF: 6.2
2023-08-26
Journal of Alloys and Compounds
Abstract:Texture and microstructure evolution of as-annealed Al-Cu-Mg-Zr cold rolled sheet (at 120–560 °C, for 1 h, with 20 °C interval) has been carefully investigated through the novel texture index and orientation streamline approach was utilized to study the dynamic rule and unknown mechanisms of texture evolution. The direct connections among texture composition, tensile performance, and microstructure were also researched. The results show that, the evident texture evolution during recovery (120–300 °C) was observed, involving Brass, Goss, and Cu. Brass T1 {φ 1 = 79°, φ = 80°, φ 2 = 10°}, Brass 70 ° {φ 1 = 70°, φ = 35°, φ 2 = 45°}, and n-Brass {φ 1 = 19°, φ = 65°, φ 2 = 27°}) are responsible for the transformation of Brass. Goss T {φ 1 = 90°, φ = 20°, φ 2 = 45°} promoted the transition of Goss; 30° relationship between Cu and α 55 ° {φ 1 = 55°, φ = 45°, φ 2 = 0°} facilitated the transformation in between. Moreover, the content of ∑3 (60° ) twin boundary and texture index weaken each other at 300–500 °C; ∑3 twin boundary contributes to the elongation, and the increase of texture index improves the tensile strength and tensile toughness. The dislocation density difference may provide the thermodynamic condition to further promote the preferential transformation between Goss texture and its twinning orientation Goss T during recovery.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering