Abstract:Highly porous and hydrophobic silica aerogel is fabricated using fly ash and trona ore as the starting materials and the cost-effective ambient pressure drying technique. The optimal calcination parameters are determined as temperature of 850°C, holding time of 2h, and the trona ore/fly ash mass ratio of 1.4. The CO2 release mechanism during calcination is proposed and has been verified by the Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) and X-ray fluorescence (XRF) technique. The hydrogel is derived from reacting the calcination mixture with sulphuric acid solution, followed by filtration. The impurities can be effectively removed through water washing and solvent exchange processes. No ion exchange resin is used in this preparation method, and thus it is a safe, inexpensive and much more straightforward process. In order to minimize drying shrinkage, the hydrogel is first transformed into an alcogel by soaking in ethanol, after which the alcogel is surface modified with the hexane/ethanol/trimethylchlorosilane (hexane/ethanol/TMCS) mixture solution. It has been observed that the specific surface area, BJH desorption pore volume, and BJH desorption average pore diameter all first increase and then decrease so that reach to the maximum values once the heat treatment temperature approaches 500°C due to the oxidation of CH3 groups on the silica skeleton surface. The final product presents special characteristics including: (1) high thermal stability for maintaining hydrophobicity up to 476°C, (2) contact angle of the as-dried silica aerogel as high as 151°, (3) silica particle size of ca. 3–6nm, agreeing well with the model as reported, (4) and the 500°C heat treated sample possessing a large specific surface area of 856.2m2/g, a large pore volume of 2.92cm3/g, and a BJH desorption average pore diameter of 17.1nm. The proposed inexpensive approach produces silica aerogel with superior properties and is a scalable-manufacturing method for large-scale industrial production.

Applications for silica aerogel products

Silica aerogel; synthesis, properties and characterization

Silica Aerogel: Synthesis and Applications

Aerogel production: Current status, research directions, and future opportunities

Breakthroughs in cost-effective, scalable production of superinsulating, ambient-dried silica aerogel and silica-biopolymer hybrid aerogels: from laboratory to pilot scale

Preparation of Silica Aerogels Via Ambient Pressure Drying

Three routes to superinsulating silica aerogel powder

Evolutionary Progress of Silica Aerogels and Their Classification Based on Composition: An Overview

Synthesis of silica aerogel films in liquid molds

Advances in multiple reinforcement strategies and applications for silica aerogel

Aerogel: Space exploration applications

Sintering of different silica aerogels

Silica aerogels with tailored chemical functionality

Ambient Pressure Drying as an Advanced Approach to the Synthesis of Silica Aerogel Composite for Building Thermal Insulation

Fabrication of flexible silica aerogel composite blankets from an aqueous fumed silica-based slurry

Insulating materials based on silica aerogel composites: synthesis, properties and application

A novel low-cost method of silica aerogel fabrication using fly ash and trona ore with ambient pressure drying technique

Synthesis of high specific surface area silica aerogel from rice husk ash via ambient pressure drying

Preparation, mechanical, acoustic and thermal properties of silica composite aerogel using wet-laid glass fiber felt as scaffold

An overview on alumina-silica-based aerogels

Fumed Silica-Derived, Ambient Dried, and Low-Cost Nanoporous Aerogel-like Monoliths for Thermal Insulation