Abstract:The design of super thermal insulation and high-temperature resistant materials for high temperature furnaces is crucial due to the energy crisis and the huge wasting. Although it is told that numerous studies have been reported about various of thermal insulation materials prepared by different methods, the applications of yttria-stabilized zirconia (YSZ) ceramic foams fabricated through tert-butyl alcohol (TBA)-based gel-casting process in bulk thermal isolators were barely to seen. In this paper, highly porous yttria-stabilized zirconia (YSZ) ceramic foams were fabricated by a novel gel-casting method using tert-butyl alcohol (TBA) as solvent and pore-forming agent. Different raw material ratio, sintering temperature and soaking time were all investigated to achieve optimal thermal insulation and mechanical properties. We can conclude that porosity drops gradually while compressive strength increases significantly with the rising temperature from 1000-1500°C. With prolonged soaking time, there is no obvious change in porosity but compressive strength increases gradually. All specimens have uniformly distributed pores with average size of 0.5-2μm and show good structural stability at high temperature. The final obtained ceramic foams displayed an outstanding ultra-low thermal conductivity property with only 200.6 °C in cold surface while the hot side was 1000 °C (hold 60 min to keep thermal balance before testing) at the thickness of 10 mm.

Hierarchically porous lanthanum zirconate foams with low thermal conductivity from particle‐stabilized foams

Enhancing the thermal insulating properties of lanthanum zirconate porous ceramics via pore structure tailoring

Anisotropic Porous Ceramic Material with Hierarchical Architecture for Thermal Insulation

High porosity and low thermal conductivity lanthanum zirconate porous ceramics via replica method

Highly Porous Zirconia Ceramic Foams with Low Thermal Conductivity from Particle‐Stabilized Foams

Lanthanum Zirconate Porous Ceramics with Controllable Secondary Pores for High-Temperature Thermal Insulation

Pyrochlore-fluorite dual-phase high-entropy ceramic foams with extremely low thermal conductivity from particle-stabilized suspension

Using nanocapsules as building blocks to fabricate organic polymer nanofoam with ultra low thermal conductivity and high mechanical strength

Porous yttria-stabilized zirconia ceramics with low thermal conductivity via a novel foam-gelcasting method

Facile Method for Preparing Hierarchical Al 2 O 3 –Glass Foam Ceramics with Superior Thermal Insulating Property

Facile Method for Preparing Hierarchical Al2O3-Glass Foam Ceramics with Superior Thermal Insulating Property.

Hollow-grained “Voronoi foam” ceramics with high strength and thermal superinsulation up to 1400 °C

Rare-Earth-Zirconate Porous High-Entropy Ceramics with Unique Pore Structures for Thermal Insulating Applications

A novel highly porous ceramic foam with efficient thermal insulation and high temperature resistance properties fabricated by gel-casting process

Ceramic foams with highly open channel structure from direct foaming method in combination with hollow spheres as pore-former.

Preparation of low thermal conductivity hierarchically porous diatomite ceramics by doped with ZrSiO4 opacifier-based foam-gelcasting method

Preparation of La2Zr2O7 composite SiO2 aerogels and their fiber-reinforced materials for thermal insulation applications

Enhanced near infrared reflectivity in hierarchical porous La2Zr2O7 microspheres produced by electro-spraying assisted phase inversion method

Ultra-high Strength ZTA Ceramic Foams with Large Amounts of Intragranular Structures Resulting from Dual-Phase Sol

Ultralight and High-Strength Bulk Alumina/zirconia Composite Ceramic Foams Through Direct Foaming Method

Fabrication of foamed ceramics with enhanced compressive strength and low thermal conductivity via a simple route