Abstract:We examined the effects of aluminum (Al) capping layer thickness on the electrical performance and stability of high-mobility indium–gallium–tin oxide (IGTO) thin-film transistors (TFTs). The Al capping layers with thicknesses (tAls) of 3, 5, and 8 nm were deposited, respectively, on top of the IGTO thin film by electron beam evaporation, and the IGTO TFTs without and with Al capping layers were subjected to thermal annealing at 200 °C for 1 h in ambient air. Among the IGTO TFTs without and with Al capping layers, the TFT with a 3 nm thick Al capping layer exhibited excellent electrical performance (field-effect mobility: 26.4 cm2/V s, subthreshold swing: 0.20 V/dec, and threshold voltage: −1.7 V) and higher electrical stability under positive and negative bias illumination stresses than other TFTs. To elucidate the physical mechanism responsible for the observed phenomenon, we compared the O1s spectra of the IGTO thin films without and with Al capping layers using X-ray photoelectron spectroscopy analyses. From the characterization results, it was observed that the weakly bonded oxygen-related components decreased from 25.0 to 10.0%, whereas the oxygen-deficient portion was maintained at 24.4% after the formation of the 3 nm thick Al capping layer. In contrast, a significant increase in the oxygen-deficient portion was observed after the formation of the Al capping layers having tAl values greater than 3 nm. These results imply that the thicker Al capping layer has a stronger gathering power for the oxygen species, and that 3 nm is the optimum thickness of the Al capping layer, which can selectively remove the weakly bonded oxygen species acting as subgap tail states within the IGTO. The results of this study thus demonstrate that the formation of an Al capping layer with the optimal thickness is a practical and useful method to enhance the electrical performance and stability of high-mobility IGTO TFTs.

Mobility and Current Boosting of In-Ga-Zn-O thin-film transistors with Metal Capping Layer Oxidation

Improved Field-Effect Mobility of In–Ga–Zn–O TFTs by Oxidized Metal Layer

Hydrogen-Doping-Enabled Boosting of the Carrier Mobility and Stability in Amorphous IGZTO Transistors

Improved high voltage operation of amorphous In-Ga-Zn-O thin film transistor by carrier density enhancement

Enhancing the Stability and Mobility of TFTs via Indium-Tungsten Oxide and Zinc Oxide Engineered Heterojunction Channels Annealed in Oxygen Ambient

Effect of high conductivity amorphous InGaZnO active layer on the field effect mobility improvement of thin film transistors

Mobility and Stability Enhancement of Amorphous In-Ga-Zn-O TFTs with Atomic Layer Deposited Al2O3/SiO2Stacked Insulators

Electrical Performance and Stability Improvements of High-Mobility Indium–Gallium–Tin Oxide Thin-Film Transistors Using an Oxidized Aluminum Capping Layer of Optimal Thickness

Improved mobility and bias stability of Hf-doped IGZO/IZO/Hf-doped IGZO thin-film transistor

Enhanced Electrical Properties and Stability in IGZO TFTs via Low-Temperature Activation with MgOx Layer

15.2: Invited Paper: Atomic Layer Deposited Oxide Semiconductor Enabling High Mobility and Low Driving Voltage in TFTs

Enhanced Stability of Solution-Processed Indium–Zinc–Tin–Oxide Transistors by Tantalum Cation Doping

Boost up mobility of solution-processed metal oxide thin-film transistors via confining structure on electron pathways.

High mobility of IGO/IGZO double-channel thin-film transistors by atomic layer deposition

Tri‐Layer Heterostructure Channel of a‐IGZO/a‐ITZO/a‐IGZO Toward Enhancement of Transport and Reliability in Amorphous Oxide Semiconductor Thin Film Transistors

A Simple Doping Process Achieved by Modifying the Passivation Layer for Self-Aligned Top-Gate In-Ga-Zn-O Thin-Film Transistors at 200 degrees C

P‐1.11: Performance Improvement of a‐IGZO Thin‐Film Transistor By Using Ta 2 O 5 /SiO 2 Double‐layer Gate Dielectric

Enhanced performances of a-IGZO TFTs with oxide passivation layers fabricated by hollow cathode assisted PLD

Enhancing the Carrier Mobility and Bias Stability in Metal–Oxide Thin Film Transistors with Bilayer InSnO/a-InGaZnO Heterojunction Structure

Influence of metallization process on solution-processed InGaZnO thin film transistors

Mobility Enhancement of BCE-Type Amorphous InGaZnO TFTs Using Triple-Layer Channels