Abstract:Al alloy joints soldered with Sn-based filler metal are susceptible to corrosion and early failure when exposed to moisture, resulting in severe accidents and substantial economic losses. This study proposes a method to prevent galvanic corrosion by separating Al alloys and Sn-based filler metals with an insulating barrier layer of anodized aluminum oxide (AAO) composed of Al2O3. The successful joining of anodized aluminum alloy (AAA) with Sn-9Zn-2Al was achieved through ultrasonic-assisted hot dipping and soldering in air at 240 degrees C. Microstructural examination revealed strong bonding between the solder alloy and AAO, with the solder infiltrating the AAO nanotubes and a transition layer consisting of two sublayers at the interface: amorphous ZnO mixed with nanocrystals (ZnO and Al2O3) and amorphous Al2O3. The shear strength of the joints ranged from 31.8 to 32.8 MPa when subjected to ultrasonic hot dipping for 0.5-2.0 s, with no significant difference observed. Fracture initiation and propagation occur within the transition layer at the interface. The shear strength of joints subjected to dipping for more than 3.0 s decreased slightly to 27.9 MPa due to localized peeling off of AAO from the Al substrate. The formation of the interface involves the segregation of Al and Zn on the liquid filler metal surface, driven by differences in atomic activity. Due to the jet force from cavitation, an Al-rich liquid infiltrates the nanotube, resulting in the formation of Zn-O at the interface and Al-O both at the interface and within the nanotube. Throughout this process, the wetting model shifts from a Cassie state to a near-Wenzel state. Immersion tests of two types of joints, Al/SnZnAl/Al and AAA/SnZnAl/AAA, confirmed that galvanic corrosion of Sn/Al was completely inhibited by the latter. Consequently, AAA joints demonstrate excellent corrosion resistance, validating this approach as a promising solution to the Al/Sn galvanic corrosion issue.

Improvement of Biocompatible TA9/ZrO2 Joint by AuSn20 Filler: Interfacial Microstructure, Mechanical Properties, and Corrosion Resistance.

Evaluation of Corrosion-Resistant TA9/ZrO2 Joint Brazed with AuSn20 and Sn6Zr Fillers: Interfacial Evolution and Mechanical Properties

Vacuum Brazing of Medical TA9 Alloy to ZrO2 Bioceramics Using a Biocompatible Filler: Interfacial Microstructure, Mechanical Properties and Biocompatibility

Low Temperature Brazing Between Pre-Metallized ZrO2 Ceramics and Medical Pure Titanium Using AuSn20 Filler Metal

Evaluation of Biomedical Ti/ZrO2 Joint Brazed with Pure Au Filler: Microstructure and Mechanical Properties

Interactions, Joining and Microstructure of Sn-Ti/ZrO2 System

Influence of microalloying with B on the microstructure and properties of brazed joints with Ag–Cu–Zn–Sn filler metal

Novel Ti–Zr–Co–Cu–M (M = Sn, V, Al) amorphous/nanocrystalline brazing fillers for joining Ti–6Al–4 V alloy

Interfacial Structure and Properties of Anodized 6061 Al Alloy Joints by Ultrasonic-Assisted Hot Dipping and Soldering Using a Sn-9Zn-2Al Filler Metal

Improve mechanical properties and corrosion resistance of Al/Sn heterogeneous joints by ultrasonic-assisted liquid phase diffusion bonding

Design of Gr/2024Al composite and Ti6Al4V titanium alloy joint brazed using AgCuSnTi filler and Ni/Nb/Ni composite interlayers

Active Brazing of Alumina and Copper with Multicomponent Ag-Cu-Sn-Zr-Ti Filler

Microstructure and Mechanical Properties of Al2O3/Cu Joints Brazed with Ag–Cu–Ti+Zn Composite Fillers

Effect of Sn element on the interfacial reinforced AlN/Cu joint brazed by Ag–Cu–Ti–(Snx) filler

Low Temperature Brazing of Biomedical Titanium and Zirconia Metallized with Sn-Ti Metal Foil

Vacuum Brazing of Biomedical TNZ Alloy to ZrO 2 Ceramic Using Sn–Zr Filler: Interfacial Microstructure and Mechanical Properties

Influence of Zr addition on TIG welding-brazing of Ti-6Al-4V toAl5A06

Improving the Mechanical Properties and Intergranular Corrosion Resistance of Al-9.2Mg-0.8Mn-0.2Zr Alloy by Sn Addition

Interfacial Microstructure and Mechanical Properties of Ultrasonic-Assisted Brazing Joints Between Ti–6Al–4V and ZrO2

Ultrasonic-assisted Brazing of Al–Ti Dissimilar Alloy by a Filler Metal with a Large Semi-Solid Temperature Range

Optimization of the Microstructure and Mechanical Properties of a TC4 Alloy Joint Brazed with a Zr-Based Filler Containing a Co Element