Abstract:<p>In this work, 7075 Al alloys were ultrasonically soldered by pure Zn solder in air under different acoustic intensities. The dependence of the microstructure and mechanical properties of joints on acoustic intensity was revealed. Acoustic intensity is innovatively controlled by applying different lap widths without increasing the input ultrasonic power. The acoustic pressure inside the solder was simulated by finite element simulation, and results showed that the acoustic intensity increased by more than six times when the lap width decreased by 50 %. High acoustic intensity led to intense cavitation, thereby causing a pronounced erosion of substrate. The Al content inside the joint increased from 17.3%–24.5% when the clearance width decreased from 0.8 mm to 0.4 mm. The Clausius–Clapeyron equation helped explain that the melting point of Zn increased by approximately 73.8 °C under the high acoustic pressure caused by cavitation bubble collapse, which could cause the direct solidification of Zn and served as the main reason of grain refinement. Zn grains were refined from 6.9 μm to 4.2 μm when soldered at 0.8 mm and further to 3.5 μm when soldered at 0.4 mm because of the strong cavitation caused by high acoustic intensity. Acoustic intensity had a remarkable effect on the mechanical properties of joints. Joint shear strength and hardness increased from 117.3 MPa and 93.3 HV to 145.1 MPa and 109.4 HV, respectively, when the lap clearance width decreased from 0.8 to 0.4 mm. Particularly, the joint soldered at 0.4 mm failed through the substrate because of the high strength of the joint seam and the weakness of the substrate, which were explained through the Hall–Patch relationship, the Schmid factor, the dissolution of secondary phases, and the increase in high angle boundaries. This work provides a novel method by producing strong joints with fine grains without increasing input power.</p>

Improve mechanical properties and corrosion resistance of Al/Sn heterogeneous joints by ultrasonic-assisted liquid phase diffusion bonding

Manufacturing high-strength and corrosion-resistant 6063Al joints by an ultrasonic-assisted liquid and solid phase diffusion technology

Ultrasonic-assisted liquid phase diffusion bonding of Al alloys under low temperature and pressure for high-temperature resistance applications

High-strength joining of 6063Al alloys by an Zn–Sn hypereutectic interlayer in air based on liquid and solid phase diffusion

Microstructure evolution and interfacial bonding mechanisms of ultrasonically soldered sapphire/Al dissimilar joints using Sn-based solders

Ni mesh-reinforced ultrasonic-assisted Cu/Sn58Bi/Cu joint performance: Experiments and first-principles calculations

Microstructure and Mechanical Properties of Ultrasonically Assisted Brazing of Dissimilar Cu–Al Alloys

Avoiding degradation and increasing joint strength of Al alloys by rapid ultrasonic soldering at low temperature

Sn-enhanced high-temperature reliability of Cu/Nano-Ag/Cu joint via transient-liquid-phase bonding

Ultrasonic semi-solid coating soldering 6061 aluminum alloys with Sn-Pb-Zn alloys

Accelerated solid-liquid interdiffusion bonding of Cu joint using a Cu10Ni alloy mesh reinforced SAC305 composite solder

Ultrasonic-Assisted Semi-Solid Forming Method and Microstructure Evolution of Aluminum/Copper Brazed Joints

Effect of Sn element on the interfacial reinforced AlN/Cu joint brazed by Ag–Cu–Ti–(Snx) filler

Tuning the microstructure and enhancing the mechanical properties of Au-20Sn/Au/Ni(P)/Kovar joint by ultrasonic-assisted soldering method

Joining mechanism, microstructure, and mechanical properties of AZ31/6061 joint prepared by pouring fusion welding process assisted with Zn-xSn brazing filler

Ultrasonic-induced metallurgical bonding between W90 tungsten heavy alloy and AZ31B Mg alloy using Sn

Mechanism of ultrasonic-assisted transient liquid phase bonding of 6061 Al alloy with cladded Zn-Al alloy in air

Improving the microstructure and mechanical properties of Al-Cu dissimilar joints by ultrasonic dynamic-stationary shoulder friction stir welding

Diffusion reaction-induced microstructure and strength evolution of Cu joints bonded with Sn-based solder containing Ni-foam

Dependence of the microstructure and properties of joints on acoustic intensity during the ultrasonic soldering of 7075 Al alloys

Rapid Ultrasonic-Assisted Soldering of AZ31B Mg Alloy/6061 Al Alloy with Low-Melting-Point Sn–xZn Solders Without Flux in Air