Mechanical Strengthening and Corrosion Behavior of Friction Stir Welded Dual-Phase Fe50Mn30Co10Cr10 High Entropy Alloy

Shulei Sun,Li Zhou,Zhaoxu Yang,Linghang Ma,Xiaoguo Song
DOI: https://doi.org/10.1016/j.msea.2024.147589
IF: 6.044
2024-01-01
Materials Science and Engineering A
Abstract:This study explores the mechanical strengthening and corrosion behavior of friction stir welded joints in dual-phase Fe50Mn30Co10Cr10 high entropy alloy (HEA). The influence of microstructural evolution on the joint's mechanical properties was analyzed, along with an assessment of its corrosion resistance using electrochemical quantitative analysis. Additionally, the corrosion mechanisms of HEAs were explored by analyzing corrosion morphology. The results show that the nugget zone exhibits a low fraction of HCP phase, yet refined grains contribute to higher hardness compared to the base metal. The presence of multiple dislocations, HCP phases, and partially fine grains enhanced hardness in thermal-mechanical affected zone and heat affected zone, despite coarse grain does not favor hardness in these zones. Although fracture occurred in the heat affected zone due to inadequate inhibition of coarse grains on the crack propagation, the TRIP effect increased the joint's tensile strength to 97.1% of the base metal. Reduced Mn segregation and grain refinement in the nugget zone promote the formation of thicker and more uniform passivation films, which exhibit superior corrosion resistance compared to the base metal. Conversely, a high fraction of HCP phase in the base metal elevated its tensile strength but reduced elongation by inducing high stress concentrations near phase boundaries. And the combined effects of component segregation, a high fraction of HCP phase, and bulk grain boundaries accelerate base material dissolution.
What problem does this paper attempt to address?