Influence of the Microstructure and Mechanical Properties of a Hypoeutectic Al-10Mg2Si in Situ Composite with Yttrium Addition

Fachang Zhao,Xingming Zhao,JinLiang Bi,Xiao Zhu,HongLin Li,Guosheng Qin,Xue Liu,Wei,Rongda Zhao,Fufa Wu

DOI: https://doi.org/10.1007/s11837-024-06947-y

2024-01-01

JOM

Abstract:Owing to their superior mechanical properties, Al-Mg2Si composite materials are widely employed in the aerospace, electronic, and automotive industries, among other fields. The microstructures of the Al-10Mg2Si composite materials with various Y contents were analyzed via x-ray diffraction (XRD), 3CCD real-color confocal microscopy (3CCD), field-emission scanning electron microscopy (SEM), and transmission electron microscopy (TEM). Concurrently, the mechanical properties were assessed through hardness and tensile testing using a microhardness tester and a universal testing machine, respectively. The experimental results demonstrated that the addition of Y to the Al-Mg2Si alloy led to the formation of three distinct phases: α-Al, Mg2Si, and Al3Y. The primary growth of the Al-10Mg2Si alloy with Y inclusion led to a refinement of the α-Al structure and a modification of the eutectic Mg2Si structure. As the Y content increased, the strength and elongation of the Al-10Mg2Si alloy initially increased, followed by a decrease. The highest tensile strength and total elongation of the Al-10Mg2Si alloy with Y addition were 320 MPa and 6.2