Abstract:This work focuses on the effect of Cu protrusion on the reliability of High Bandwidth Memory (HBM) fabricated by wafer-to-wafer hybrid bonding (W2W-HB) process. The thermal stress induced by large coefficient of thermal expansion (CTE) mismatch between different materials could seriously deteriorate the device performance, and even lead to failure. Different manufacturing and service conditions could greatly affect the microstructure and deformation behavior of the through silicon via (TSV). In this paper, a new process was designed to realize the self-compensation of the surface topology by rationally utilizing the dishing defects caused by CMP. The influence of dielectric materials (dielectric layer thickness and CTE) on Cu protrusion height was systematically explored. A finite element analysis (FEA) model was proposed to provide insight into the Cu protrusion mechanism under different operating conditions. Annealing tests were carried out to identify how the microstructure affects protrusion and to verify the accuracy of the model. During the test, the extruded TSV was observed using scanning electron microscopy (SEM) and atomic force microscopy (AFM). Mechanisms of Cu protrusion in TSVs during heat treatment were analyzed, and possible factors involving thermal stress were discussed through the model. In addition, debonding risk was evaluated by comparing the peak interfacial peeling stress and the protrusion height for various scenarios. The conclusions can be used to understand and solve the key issues in the reliability challenges of HBM W2W-HB stacking process by enabling high-throughput TSV fabrication.

Simulation and Experimental Analysis of Thermomechanical Stress Around Interconnects for W2W Hybrid Bonding

Transient Electro-Thermo-mechanical Responses of Wire Bonding Interconnects Illuminated by an Electromagnetic Pulse

Hybrid Physical Field Simulation: Transient Electro-Thermo-Mechanical Responses Of Interwafer Interconnects Under The Impact Of An Emp

Wafer-to-Wafer Hybrid Bonding Development by Advanced Finite Element Modeling for 3-D IC Packages

Modelling and characterization on wafer to wafer hybrid bonding technology for 3D IC packaging

Research on Simulation of Cu/SiO2 Hybrid Bonding Process and Interface Failure Mechanism by Finite Element Analysis

Reliability Analysis of Bonding Wire Based on Stacked Substrate Packaging Structure

Modeling and Analysis of Transmission Performance of Bonding Wire Interconnection

Simulation Analysis of Mechanical Response of Wire Bonding in SiP under Thermal-mechanical-electrical Coupling Load

Thermal Finite Element Simulation of Ultrafine Pitch Chip-to-Wafer Hybrid Bonding

Optimization of Cu protrusion of wafer-to-wafer hybrid bonding for HBM packages application

Thermal Stress Analysis of Wafer-Level Multilayer Stacking Process for 3D-TSV Packaging

Modeling of interconnect stress evolution during BEOL process and packaging

Influences of Material and Structural Factors on the Stress Conditions in Cu/low-k Chips During Cu Wire Bonding

Analytical Modeling of Thermo-Mechanical Stress for Bond Wire of IGBT Module

Stress analysis of interconnect structure in COF by finite element method

Simulation of Stress for Cu Interconnects

Board level FEA reliability and stress modeling for chip-to-wafer bonded chiplet package

Multiphysics Simulation of Chiplet Integration Process-Induced Stress Effects on AC and DC Quantum Transport of FinFET from System Technology Co-Optimization Perspective

Stress Evolution Mechanism and Thermo-Mechanical Reliability Analysis of Copper-Filled TSV Interposer

A Method to Improve 3D Interconnections Resource Utilization and Reliability in Hybrid Bonding Process Considering the Effects on Signal Integrity